Phase change inks

ABSTRACT

Disclosed is a phase change ink composition comprising a phase change ink carrier and a colorant compound of the formula  
                 
 
     wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R 1  is an alkylene group or an arylalkylene group, and X is (a) a hydrogen atom, (b) a group of the formula  
                 
 
     wherein R 2  is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (c) an alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, or (d) a group of the formula  
                 
 
     wherein R 4  is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.

[0001] Cross-reference is made to the following copending applications:

[0002] Copending Application U.S. Ser. No. ______ (not yet assigned; Attorney Docket No. D/A2341), filed concurrently herewith, entitled “Colorant Compounds,” with the named inventors Jeffery H. Banning and C. Wayne Jaeger, the disclosure of which is totally incorporated herein by reference, discloses compounds of the formula

[0003] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, and X is (a) a hydrogen atom, (b) a group of the formula

[0004] wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (c) an alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, or (d) a group of the formula

[0005] wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.

[0006] Copending Application U.S. Ser. No. ______ (not yet assigned; Attorney Docket No. D/A2341Q1), filed concurrently herewith, entitled “Methods for Making Colorant Compounds,” with the named inventors C. Wayne Jaeger and Jeffery H. Banning, the disclosure of which is totally incorporated herein by reference, discloses a process for preparing a colorant of the formula

[0007] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, and R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, can be prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0008] followed by (b) converting the colorant thus prepared to either (i) an ester-substituted colorant by reaction with an esterification compound which is either (A) an anhydride of the formula

[0009] or (B) an acid of the formula R₂COOH in the presence of an optional esterification catalyst, or (ii) a urethane-substituted colorant by reaction with an isocyanate compound of the formula

R₄—N═C═O

[0010] and (c) brominating the colorant thus prepared, wherein either conversion to ester or urethane can be performed before bromination or bromination can be performed before conversion to ester or urethane.

BACKGROUND OF THE INVENTION

[0011] The present invention is directed to phase change inks. More specifically, the present invention is directed to hot melt or phase change inks containing specific colorant compounds. One embodiment of the present invention is directed to a phase change ink composition comprising a phase change ink carrier and a colorant compound of the formula

[0012] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, and X is (a) a hydrogen atom, (b) a group of the formula

[0013] wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (c) an alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, or (d) a group of the formula

[0014] wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.

[0015] In general, phase change inks (sometimes referred to as “hot melt inks”) are in the solid phase at ambient temperature, but exist in the liquid phase at the elevated operating temperature of an ink jet printing device. At the jet operating temperature, droplets of liquid ink are ejected from the printing device and, when the ink droplets contact the surface of the recording substrate, either directly or via an intermediate heated transfer belt or drum, they quickly solidify to form a predetermined pattern of solidified ink drops. Phase change inks have also been used in other printing technologies, such as gravure printing, as disclosed in, for example, U.S. Pat. No. 5,496,879 and German Patent Publications DE 4205636AL and DE 4205713AL, the disclosures of each of which are totally incorporated herein by reference.

[0016] Phase change inks for color printing typically comprise a phase change ink carrier composition which is combined with a phase change ink compatible colorant. In a specific embodiment, a series of colored phase change inks can be formed by combining ink carrier compositions with compatible subtractive primary colorants. The subtractive primary colored phase change inks can comprise four component dyes, namely, cyan, magenta, yellow and black, although the inks are not limited to these four colors. These subtractive primary colored inks can be formed by using a single dye or a mixture of dyes. For example, magenta can be obtained by using a mixture of Solvent Red Dyes or a composite black can be obtained by mixing several dyes. U.S. Pat. No. 4,889,560, U.S. Pat. No. 4,889,761, and U.S. Pat. No. 5,372,852, the disclosures of each of which are totally incorporated herein by reference, teach that the subtractive primary colorants employed can comprise dyes from the classes of Color Index (C.I.) Solvent Dyes, Disperse Dyes, modified Acid and Direct Dyes, and Basic Dyes. The colorants can also include pigments, as disclosed in, for example, U.S. Pat. No. 5,221,335, the disclosure of which is totally incorporated herein by reference. U.S. Pat. No. 5,621,022, the disclosure of which is totally incorporated herein by reference, discloses the use of a specific class of polymeric dyes in phase change ink compositions.

[0017] Phase change inks have also been used for applications such as postal marking and industrial marking and labelling.

[0018] Phase change inks are desirable for ink jet printers because they remain in a solid phase at room temperature during shipping, long term storage, and the like. In addition, the problems associated with nozzle clogging as a result of ink evaporation with liquid ink jet inks are largely eliminated, thereby improving the reliability of the ink jet printing. Further, in phase change ink jet printers wherein the ink droplets are applied directly onto the final recording substrate (for example, paper, transparency material, and the like), the droplets solidify immediately upon contact with the substrate, so that migration of ink along the printing medium is prevented and dot quality is improved.

[0019] Compositions suitable for use as phase change ink carrier compositions are known. Some representative examples of references disclosing such materials include U.S. Pat. No. 3,653,932, U.S. Pat. No. 4,390,369, U.S. Pat. No. 4,484,948, U.S. Pat. No. 4,684,956, U.S. Pat. No. 4,851,045, U.S. Pat. No. 4,889,560, U.S. Pat. No. 5,006,170, U.S. Pat. No. 5,151,120, U.S. Pat. No. 5,372,852, U.S. Pat. No. 5,496,879, European Patent Publication 0187352, European Patent Publication 0206286, German Patent Publication DE 4205636AL, German Pafent Publication DE 4205713AL, and PCT Patent Application WO 94/04619, the disclosures of each of which are totally incorporated herein by reference. Suitable carrier materials can include paraffins, microcrystalline waxes, polyethylene waxes, ester waxes, fatty acids and other waxy materials, fatty amide containing materials, sulfonamide materials, resinous materials made from different natural sources (tall oil rosins and rosin esters, for example), and many synthetic resins, oligomers, polymers, and copolymers.

[0020] U.S. Pat. No. 6,395,078 (Jaeger), U.S. Pat. No. 6,422,695 (Jaeger), Canadian Patent Publication 2 355 533 (filed Aug. 20, 2001, published Feb. 23, 2002), European Patent Publication EP 1 182 232 (filed Aug. 17, 2001, published Feb. 27, 2001), Japanese Patent Publication JP 2002129044 (filed Aug. 8, 2001, published May 9, 2002), Brazilian Patent Publication P101035819 (filed Aug. 22, 2001, published Mar. 26, 2002), and Mexican Patent Application 2001008418 (filed Aug. 20, 2001), the disclosures of each of which are totally incorporated herein by reference, disclose a compound having the formula

[0021] wherein at least one Q₁, Q₂, Q₃, and Q₄ is a halogen atom and any of Q₁, Q₂, Q₃ and Q₄ which is not a halogen atom is a hydrogen atom; and wherein R comprises at least two carbon atoms. The invention further encompasses inclusion of such compound into phase change ink carrier compositions, as well as printing methods utilizing such compound.

[0022] British Patent Publication GB 2 021 138 (Hohmann et al.), the disclosure of which is totally incorporated herein by reference, discloses mixtures of dyestuffs of the formula

[0023] and of the formula

[0024] wherein R₁, R₂, and R₃ denote C₁-C₄ alkyl, C₁-C₄ alkoxy, or halogen, and n denotes 2 or 3, which are suitable for dyeing polyester fibers by the exhaustion process. Dark blue and navy blue dyeings with good fastness properties are obtained.

[0025] U.S. Pat. No. 6,174,937 (Banning et al.), the disclosure of which is totally incorporated herein by reference, discloses a phase change ink comprising a material of the formula

[0026] wherein X₁, X₂, X₃ and X₄ are segments comprising atoms selected from groups V and VI of the periodic table; wherein at least one R₁ and R₅ comprises at least 37 carbon units; and wherein R₂, R₃ and R₄ each comprise at least one carbon unit. The invention further encompasses a composition of matter, as well as methods of reducing coefficients of friction of phase change ink formulations.

[0027] U.S. Pat. No. 5,507,864 (Jaeger et al.), the disclosure of which is totally incorporated herein by reference, discloses a phase change ink composition that includes a combination of different dye types such as an anthraquinone dye and a xanthene dye, which is most preferably a rhodamine dye. While each dye type is insufficiently soluble with respect to favored carrier compositions to preserve color saturation in reduced ink quantity prints, the dye type combination permits increased dye loading and maintains print quality. In a preferred embodiment of the invention, a favored carrier composition is adjusted to promote the colored form of a preferred rhodamine dye (C.I. Solvent Red 49) and mixed with a preferred anthraquinone dye (C.I. Solvent Red 172) whose concentration is kept below a critical level to prevent post printed blooming. The resulting preferred phase change ink compositions provide a magenta phase change ink with enhanced light fastness and color saturation, as well as good compatibility with preferred existing subtractive primary color phase change inks.

[0028] U.S. Pat. No. 5,902,841 (Jaeger et al.), the disclosure of which is totally incorporated herein by reference, discloses a phase change ink composition wherein the ink composition utilizes a colorant in combination with a selected phase change ink carrier composition containing at least one hydroxy-functional fatty amide compound.

[0029] R. Butnaru et al., “Researches on Dyeing of Cotton Fabrics with Acid Dyestuffs, Concomitantly with Crease-Resist Treatments,” Cellulose Chem. Technol., 29, p. 471 (1995), the disclosure of which is totally incorporated herein by reference, discloses an analysis of the results obtained on dyeing of cotton cellulosic fabrics with acid dyestuffs, on employing crease-resist agents with polyfunctional structure. The conclusion was reached that no chemical or physical bonds occur between dyestuffs and the fiber, the dyestuffs being fixed onto the resin's aminic groups formed as a result of the thermal, crease-resist treatment. Washing resistance of the cellulosic materials thus dyed attained the values obtained as a result of dyeing with direct dyestuffs, specific for these types of fibers.

[0030] U.S. Pat. No. 6,235,094 (Banning et al.), the disclosure of which is totally incorporated herein by reference, discloses a compound having the formula

[0031] wherein R₁, Z and the carbonyl can be comprised by a common ring, wherein R₁ comprises a chromophore that absorbs light from the visible wavelength range, and wherein n is an integer that is at least 12. The invention also encompasses a solid phase change ink composition. Such composition includes a phase change ink carrier and a colorant. The colorant comprises a chromophore that absorbs light from the visible wavelength range, and has the formula

[0032] wherein R₁, Z and the carbonyl can be comprised by a common ring, wherein n is an integer that is at least 12. Additionally, the invention encompasses a method of forming a colorant. A first compound having the formula

[0033] is reacted with a second compound having the formula Z(CH₂)_(n)CH₃, wherein n is an integer that is at least 12, to form a third compound having the formula

[0034] wherein the third compound comprises a chromophore that absorbs light from the visible wavelength range.

[0035] While known compositions and processes are suitable for their intended purposes, a need remains for improved colorant compounds. In addition, a need remains for colorant compositions particularly suitable for use in phase change inks. Further, a need remains for colorant compounds with a desirable magenta color. Additionally, a need remains for colorant compounds with desirable thermal stability. There is also a need for colorant compounds with good lightfastness. In addition, there is a need for colorant compounds that exhibit desirable solubility characteristics in phase change ink carrier compositions. Further, there is a need for colorant compounds that, when incorporated into phase change inks, exhibit reduced migration within a layer of printed ink. Additionally, there is a need for colorant compounds that, when incorporated into phase change inks, exhibit reduced crystallization within a layer of printed ink. A need also remains for colorant compounds that, when incorporated into phase change inks, enable production of prints that maintain uniform color over long periods of time without unevenness or blotching. In addition, a need remains for colorant compounds that, when incorporated into phase change inks, enable production of prints that retain their original color over long periods of time. Further, a need remains for colorant compounds that, when incorporated into phase change inks, enable production of prints that exhibit reduced sensitivity to image discoloration upon contact with human fingertips. Additionally, a need remains for colorant compounds that can be incorporated into phase change inks in desirably high concentrations. There is also a need for colorant compounds that can be manufactured easily and practically. In addition, there is a need for colorant compounds that can easily be converted to derivative molecules thereof.

SUMMARY OF THE INVENTION

[0036] The present invention is directed to a phase change ink composition comprising a phase change ink carrier and a colorant compound of the formula

[0037] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, and X is (a) a hydrogen atom, (b) a group of the formula

[0038] wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (c) an alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, or (d) a group of the formula

[0039] wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.

DETAILED DESCRIPTION OF THE INVENTION

[0040] The present invention is directed to phase change ink compositions comprising a phase change ink carrier and a colorant compound of the formula

[0041] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group (including linear, branched, saturated, unsaturated, cyclic, and unsubstituted alkylene groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the alkylene group), in one embodiment with at least about 1 carbon atom, and in another embodiment with at least about 2 carbon atoms, and in one embodiment with no more than about 50 carbon atoms, in another embodiment with no more than about 20 carbon atoms, in yet another embodiment with no more than about 6 carbon atoms, and in still another embodiment with no more than about 2 carbon atoms, although the number of carbon atoms can be outside of these ranges, or an arylalkylene group (including unsubstituted and substituted arylalkylene groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the arylalkylene group), in one embodiment with at least about 6 carbon atoms, and in another embodiment with at least about 7 carbon atoms, and in one embodiment with no more than about 50 carbon atoms, in another embodiment with no more than about 20 carbon atoms, in yet another embodiment with no more than about 7 carbon atoms, although the number of carbon atoms can be outside of these ranges, and X is (a) a hydrogen atom, (b) a group of the formula

[0042] wherein R₂ is an alkyl group (including linear, branched, saturated, unsaturated, cyclic, unsubstituted, and substituted alkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the alkyl group), in one embodiment with at least about 1 carbon atom, in another embodiment with at least about 2 carbon atoms, in another embodiment with at least about 4 carbon atoms, in yet another embodiment with at least about 6 carbon atoms, in still another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 70 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an aryl group (including unsubstituted and substituted aryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the aryl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 13 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least a bout 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 75 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an arylalkyl group (including unsubstituted and substituted arylalkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the arylalkyl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, or an alkylaryl group (including unsubstituted and substituted alkylaryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the alkylaryl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, (c) an alkyleneoxy group, an aryleneoxy group, an arylalkyleneoxy group, or an alkylaryleneoxy group, including (but not limited to) those of the formula

—(C_(a)H_(2a)O)_(b)R₃

[0043] wherein a is an integer representing the number of carbon atoms in the alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, being in various embodiments 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, or 50, although the value of a can be outside of these ranges, b is an integer representing the number of repeat alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy groups, being in one embodiment at least 1, in another embodiment at least about 2, in yet another embodiment at least about 5, and in still another embodiment at least about 10, and being in one embodiment no more than about 200, in another embodiment no more than about 150, in yet another embodiment no more than about 100, and in still another embodiment no more than about 50, although the value of b can be outside of these ranges, and R₃ is a hydrogen atom, an alkyl group (including linear, branched, saturated, unsaturated, cyclic, unsubstituted, and substituted alkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the alkyl group), in one embodiment with at least about 1 carbon atom, in another embodiment with at least about 2 carbon atoms, in another embodiment with at least about 4 carbon atoms, in yet another embodiment with at least about 6 carbon atoms, in still another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 70 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an aryl group (including unsubstituted and substituted aryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the aryl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 13 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 75 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an arylalkyl group (including unsubstituted and substituted arylalkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the arylalkyl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, or an alkylaryl group (including unsubstituted and substituted alkylaryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the alkylaryl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, or (d) a group of the formula

[0044] wherein R₄ is an alkyl group (including linear, branched, saturated, unsaturated, cyclic, unsubstituted, and substituted alkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the alkyl group), in one embodiment with at least about 1 carbon atom, in another embodiment with at least about 2 carbon atoms, in another embodiment with at least about 4 carbon atoms, in yet another embodiment with at least about 6 carbon atoms, in still another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with a t least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 70 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an aryl group (including unsubstituted and substituted aryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the aryl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 13 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 75 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an arylalkyl group (including unsubstituted and substituted arylalkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the arylalkyl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an alkylaryl group (including unsubstituted and substituted alkylaryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the alkylaryl group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, wherein the substituents on the substituted alkyl, alkylene, aryl, arylene, arylalkyl, arylalkylene, alkylaryl, and alkylarylene groups can be (but are not limited to) hydroxy groups, halogen atoms, amine groups, imine groups, ammonium groups, cyano groups, pyridine groups, pyridinium groups, ether groups, aldehyde groups, ketone groups, ester groups, amide groups, carbonyl groups, thiocarbonyl groups, sulfate groups, sulfonate groups, sulfide groups, sulfoxide groups, phosphine groups, phosphonium groups, phosphate groups, nitrile groups, mercapto groups, nitro groups, nitroso groups, sulfone groups, acyl groups, acid anhydride groups, azide groups, azo groups, cyanato groups, isocyanato groups, thiocyanato groups, isothiocyanato groups, mixtures thereof, and the like, wherein two or more substituents can be joined together to form a ring.

[0045] The above formula encompasses monomeric materials. In addition, the above formula encompasses dimeric materials containing two moieties of the formula

[0046] linked by a central X moiety, as follows:

[0047] wherein Y and Y′ each, independently of the other, is a hydrogen atom or a bromine atom, n and n′ each, independently of the other, is an integer of 0, 1, 2, 3, or 4, R₁ and R₁′ each, independently of the other, is an alkylene group or an arylalkylene group as defined in further detail for the alkylene and arylalkylene R₁ groups hereinabove, and X is (a) a group of the formula

[0048] wherein R₂ is an alkylene group, an arylene group, an arylalkylene group, or an alkylarylene group as defined in further detail for the alkyl, aryl, arylalkyl, and alkylaryl R₂ groups hereinabove, (b) an alkyleneoxy group, an aryleneoxy group, an arylalkyleneoxy group, or an alkylaryleneoxy group as defined in further detail for the alkyleneoxy, aryleneoxy, arylalkyleneoxy, and alkylaryleneoxy R₂ groups hereinabove, or (c) a group of the formula

[0049] wherein R₄ is an alkylene group, an arylene group, an arylalkylene group, or an alkylarylene group as defined in further detail for the alkyl, aryl, arylalkyl, and alkylaryl R₄ groups hereinabove. For example, when the colorant material is formed from a diacid starting material of the formula

HOOC—R₂—COOH

[0050] wherein R₂ is as defined hereinabove, X is of the formula

[0051] When X is an alkyleneoxy group, an aryleneoxy group, an arylalkyleneoxy group, or an alkylaryleneoxy group, it can be of the formula

—R₃(C_(a)H_(2a)O)_(b)R₃′—

[0052] wherein a and b are as defined hereinabove when X is an alkyleneoxy group, an aryleneoxy group, an arylalkyleneoxy group, or an alkylaryleneoxy group and R₃ and R₃′ each, independently of the others, is an alkylene group (including linear, branched, saturated, unsaturated, cyclic, unsubstituted, and substituted alkylene groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the alkylene group), in one embodiment with at least about 1 carbon atom, in another embodiment with at least about 2 carbon atoms, in another embodiment with at least about 4 carbon atoms, in yet another embodiment with at least about 6 carbon atoms, in still another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 70 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an arylene group (including unsubstituted and substituted arylene groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the arylene group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 13 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in still another embodiment with at least about 38 carbon atoms, in another embodiment with at least about 40 carbon atoms, in yet another embodiment with at least about 42 carbon atoms, in still another embodiment with at least about 44 carbon atoms, in another embodiment with at least about 46 carbon atoms, in yet another embodiment with at least about 48 carbon atoms, and in still another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 100 carbon atoms, in another embodiment with no more than about 75 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, an arylalkylene group (including unsubstituted and substituted arylalkylene groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the arylalkylene group), in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, or an alkylarylene group (including unsubstituted and substituted alkylarylene groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the alkylarylene group); in one embodiment with at least about 6 carbon atoms, in another embodiment with at least about 7 carbon atoms, in yet another embodiment with at least about 8 carbon atoms, in another embodiment with at least about 10 carbon atoms, in yet another embodiment with at least about 12 carbon atoms, in still another embodiment with at least about 14 carbon atoms, in another embodiment with at least about 16 carbon atoms, in yet another embodiment with at least about 18 carbon atoms, in still another embodiment with at least about 20 carbon atoms, in another embodiment with at least about 22 carbon atoms, in yet another embodiment with at least about 24 carbon atoms, in still another embodiment with at least about 26 carbon atoms, in another embodiment with at least about 28 carbon atoms, in yet another embodiment with at least about 30 carbon atoms, in still another embodiment with at least about 32 carbon atoms, in another embodiment with at least about 34 carbon atoms, in yet another embodiment with at least about 36 carbon atoms, in another embodiment with at least about 38 carbon atoms, in yet another embodiment with at least about 40 carbon atoms, in still another embodiment with at least about 42 carbon atoms, in another embodiment with at least about 44 carbon atoms, in yet another embodiment with at least about 46 carbon atoms, in still another embodiment with at least about 48 carbon atoms, and in another embodiment with at least about 50 carbon atoms, and in one embodiment with no more than about 200 carbon atoms, in another embodiment with no more than about 100 carbon atoms, in yet another embodiment with no more than about 60 carbon atoms, and in still another embodiment with no more than about 50 carbon atoms, although the number of carbon atoms can be outside of these ranges, wherein the substituents on the substituted alkylene, arylene, arylalkylene, and alkylarylene groups can be (but are not limited to) hydroxy groups, halogen atoms, amine groups, imine groups, ammonium groups, cyano groups, pyridine groups, pyridinium groups, ether groups, aldehyde groups, ketone groups, ester groups, amide groups, carbonyl groups, thiocarbonyl groups, sulfate groups, sulfonate groups, sulfide groups, sulfoxide groups, phosphine groups, phosphonium groups, phosphate groups, nitrile groups, mercapto groups, nitro groups, nitroso groups, sulfone groups, acyl groups, acid anhydride groups, azide groups, azo groups, cyanato groups, isocyanato groups, thiocyanato groups, isothiocyanato groups, mixtures thereof, and the like, wherein two or more substituents can be joined together to form a ring.

[0053] When the colorant material is formed from a diisocyanate starting material of the formula

O═C═N—R₄—N═C═O

[0054] wherein R₄ is as defined hereinabove, X is of the formula

[0055] Similarly, the above formula encompasses trimeric, tetrameric, and higher moieties as well as oligomeric materials and polymeric materials, said materials containing three or more moieties of the formula

[0056] wherein each Y, independently of the others, is a hydrogen atom or a bromine atom, each n, independently of the others, is an integer of 0, 1, 2, 3, or 4, and each R₁, independently of the others, is an alkylene group or an arylalkylene group, said moieties being linked by a central atom or group of atoms or bonded to a polymeric chain. These materials can be made by processes analogous to those illustrated herein for the monomeric and dimeric compounds of the present invention.

[0057] Colorant compounds of the present invention can be prepared by any desired or effective method.

[0058] In one embodiment, colorant compounds of the present invention are prepared by a process for preparing a colorant of the formula

[0059] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, and R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, can be prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0060] followed by (b) converting the colorant thus prepared to either (i) an ester-substituted colorant by reaction with an esterification compound which is either (A) an anhydride of the formula

[0061] or (B) an acid of the formula R₂COOH in the presence of an optional esterification catalyst, or (ii) a urethane-substituted colorant by reaction with an isocyanate compound of the formula

R₄—N═C═O

[0062] and (c) brominating the colorant thus prepared, wherein either conversion to ester or urethane can be performed before bromination or bromination can be performed before conversion to ester or urethane.

[0063] In another embodiment, colorant compounds of the present invention are prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0064] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) a solvent, and (3) a first esterification compound which is either (i) an anhydride of the formula

[0065] wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, or (ii) an acid of the formula R₂COOH in the presence of an optional esterification catalyst, and heating the second reaction mixture to form a first ester-substituted colorant of the formula

[0066] (c) forming a third reaction mixture by admixing (1) the first ester-substituted colorant, (2) bromine, and (3) a solvent followed by quenching the third reaction mixture with water to form a brominated ester-substituted colorant and a salt thereof, of the formulae

[0067] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 1, 2, 3, or 4; (d) preparing a fourth reaction mixture by admixing (1) the brominated ester-substituted colorant and the salt thereof, (2) a base, (3) water, and (4) a solvent and heating the fourth reaction mixture to form a brominated alcohol-substituted colorant of the formula

[0068] and (e) preparing a fifth reaction mixture by admixing (1) the brominated alcohol-substituted colorant, (2) a second esterification compound which is either (i) an anhydride of the formula

[0069] wherein R₂′ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, and wherein R₂′ is different from R₂, or (ii) an acid of the formula R₂′COOH in the presence of an optional esterification catalyst, and (3) a solvent and heating the fifth reaction mixture to form a second ester-substituted colorant of the formula

[0070] In this embodiment, R₂′ has the same definitions as provided hereinabove for R₂ except that R₂′ is different from R₂.

[0071] In yet another embodiment, colorant compounds of the present invention are prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0072] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) a carboxylic acid of the formula R₂COOH, wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (3) an optional esterification catalyst, and (4) a solvent and heating the second reaction mixture to form an ester-substituted colorant of the formula

[0073] and (c) forming a third reaction mixture by admixing (1) the ester-substituted colorant, (2) bromine, and (3) a solvent followed by quenching the third reaction mixture with water to form a brominated ester-substituted colorant and a salt thereof, of the formulae

[0074] and

[0075] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 1, 2, 3, or 4.

[0076] In still another embodiment, colorant compounds of the present invention are prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0077] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) bromine, and (3) a solvent followed by quenching the second reaction mixture with water to form a brominated alcohol-substituted colorant and a salt thereof, of the formulae

[0078] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 0, 1, 2, 3, or 4; and (c) forming a third reaction mixture by admixing (1) the brominated alcohol-substituted colorant, (2) a carboxylic acid of the formula R₂COOH, wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (3) an optional esterification catalyst, and (4) a solvent and heating the third reaction mixture to form a brominated ester-substituted colorant of the formula

[0079] In yet still another embodiment, colorant compounds of the present invention are prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0080] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) an isocyanate of the formula

R₄—N═C═O

[0081] wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, and (3) an optional catalyst and heating the second reaction mixture to form a urethane-substituted colorant of the formula

[0082] and (c) forming a third reaction mixture by admixing (1) the urethane-substituted colorant, (2) bromine, and (3) a solvent followed by quenching the third reaction mixture with water to form a brominated urethane-substituted colorant and a salt thereof, of the formulae

[0083] and

[0084] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 1, 2, 3, or 4.

[0085] In still yet another embodiment, colorant compounds of the present invention are prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0086] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) bromine, and (3) a solvent followed by quenching the second reaction mixture with water to form a brominated alcohol-substituted colorant and a salt thereof, of the formulae

[0087] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 0, 1, 2, 3, or 4; and (c) forming a third reaction mixture by admixing (1) the brominated alcohol-substituted colorant, (2) an isocyanate of the formula

R₄—N═C═O

[0088] wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, and (3) an optional catalyst and heating the second reaction mixture to form a brominated urethane-substituted colorant and a salt thereof, of the formulae

[0089] An alcohol-substituted colorant of the present invention of the formula

[0090] can be prepared by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is as defined hereinabove, (3) boric acid, and (4) an optional solvent, followed by heating this reaction mixture to reflux temperature as follows (illustrated for an embodiment wherein the aminobenzene is substituted with the alcohol group in the 4- or para-position):

[0091] While quinizarin is shown above as the starting material, the presence of leucoquinizarin, which is the reduced form of quinizarin, is needed to condense with the alcohol-substituted amine. The reaction between the amine and the leucoquinizarin further reduces some of the quinizarin present in the reaction mixture to leucoquinizarin, thereby rendering it capable of reacting with more of the amine and furthering the reaction to completion. If desired, the reaction can be carried out solely with leucoquinizarin and with no quinizarin, although for economical purposes such a procedure is often not desirable. In addition, instead of adding leucoquinizarin to a reaction mixture of quinizarin and the alcohol-substituted amine, leucoquinizarin can be generated in situ by preparing a reaction mixture of quinizarin and the alcohol-substituted amine and adding to the reaction mixture a reducing agent, as disclosed in, for example, Waring and Hallas, The Chemistry and Application of Dyes, ISBN 0-306-43278-1, Plenum Publishing Co. (New York 1990), the disclosure of which is totally incorporated herein by reference.

[0092] The quinizarin and the leucoquinizarin are present in any desired or effective relative amounts, in one embodiment at least about 5 moles of leucoquinizarin per every 95 moles of quinizarin, in another embodiment at least about 2 moles of leucoquinizarin per every 3 moles of quinizarin, and in yet another embodiment at least about 1 mole of leucoquinizarin per every 1 mole of quinizarin, and in one embodiment up to 100 percent leucoquinizarin and no quinizarin, although the relative amounts of quinizarin and leucoquinizarin can be outside of these ranges.

[0093] The alcohol-substituted aminobenzene is present in any desired or effective amount, in one embodiment at least about 0.95 mole of alcohol-substituted aminobenzene per every one mole of (quinizarin plus leucoquinizarin), and in another embodiment at least about 1 mole of alcohol-substituted aminobenzene per every one mole of (quinizarin plus leucoquinizarin), and in one embodiment no more than about 1.05 moles of alcohol-substituted aminobenzene per every one mole of (quinizarin plus leucoquinizarin), and in another embodiment no more than about 1 mole of alcohol-substituted aminobenzene per every one mole of (quinizarin plus leucoquinizarin), although the amount of alcohol-substituted aminobenzene can be outside of these ranges.

[0094] The boric acid, which functions as a catalyst in the reaction between the alcohol-substituted aminobenzene and the leucoquinizarin, is present in any desired or effective amount, in one embodiment about 1 mole of boric acid per every one mole of (quinizarin plus leucoquinizarin), although the amount of boric acid can be higher or lower than this amount.

[0095] When the optional solvent is present, any desired or effective solvent can be used. Examples of suitable solvents include methanol, ethanol, isopropanol, butanol, ethylene glycol monomethyl ether, ethylene glycol dimethyl ether, and the like, as well as mixtures thereof. The reactants are present in the solvent in any desired or effective amount, in one embodiment at least about 25 grams of alcohol-substituted aminobenzene per every one liter of solvent, in another embodiment at least about 50 grams of alcohol-substituted aminobenzene per every one liter of solvent, and in another embodiment at least about 100 grams of alcohol-substituted aminobenzene per every one liter of solvent, and in one embodiment no more than about 500 grams of alcohol-substituted aminobenzene per every one liter of solvent, in another embodiment no more than about 250 grams of alcohol-substituted aminobenzene per every one liter of solvent, and in yet another embodiment no more than about 125 grams of alcohol-substituted aminobenzene per every one liter of solvent, although the amount of solvent can be outside of these ranges.

[0096] The reaction mixture containing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is as defined hereinabove, (3) boric acid, and (4) an optional solvent is heated to any desirable or effective temperature, typically the reflux temperature of the selected solvent when a solvent is used, in one embodiment at least about 50° C., in another embodiment at least about 60° C., and in yet another embodiment at least about 75° C., and in one embodiment no more than about 150° C., in another embodiment no more than about 120° C., and in yet another embodiment no more than about 80° C., although the temperature can be outside of these ranges.

[0097] The reaction mixture containing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is as defined hereinabove, (3) boric acid, and (4) an optional solvent is heated for any desirable or effective period of time, in one embodiment at least about 3 hours, and in another embodiment at least about 4 hours, and in one embodiment no more than about 24 hours, although the heating time can be outside of these ranges.

[0098] Upon completion of the reaction, the alcohol-substituted colorant according to the present invention is formed as a solid and can be recovered by cooling and filtering the reaction mixture.

[0099] The alcohol-substituted colorant according to the present invention can be converted to an ester-substituted colorant according to the present invention of the formula

[0100] by preparing a reaction mixture by admixing (1) the alcohol-substituted colorant, (2) a solvent, and (3) an esterification compound such as an anhydride of the formula

[0101] in which reaction mixture upon heating is formed an ester-substituted colorant according to the present invention as follows (illustrated for an embodiment wherein the alcohol-substituted colorant is substituted with the alcohol group in the 4- or para-position):

[0102] The alcohol-substituted colorant and the anhydride are present in any desired or effective relative amounts, in one embodiment at least about 1 mole of anhydride per every one mole of alcohol-substituted colorant, and in one embodiment no more than about 1.1 moles of anhydride per every one mole of alcohol-substituted colorant, although the amount of anhydride can be outside of these ranges.

[0103] Examples of suitable solvents include acetic acid, propionic acid, formic acid, butyric acid, dimethyl formamide, dimethyl sulfoxide, hexamethyl phosphorus triamide (HMPA), tetrahydrofuran, or the like, as well as mixtures thereof. The solvent is present in any desired or effective amount, in one embodiment at least about 25 grams of alcohol-substituted colorant per every one liter of solvent, and in another embodiment at least about 100 grams of alcohol-substituted colorant per every one liter of solvent, and in one embodiment no more than about 200 grams of alcohol-substituted colorant per every one liter of solvent, although the amount of solvent can be outside of these ranges.

[0104] The reaction mixture containing the alcohol-substituted colorant, the solvent, and the anhydride is heated to any desirable or effective temperature, in one embodiment at least about 25° C., and in another embodiment at least about 40° C., and in one embodiment no more than about 100° C., and in another embodiment no more than about 60° C., although the temperature can be outside of these ranges.

[0105] The reaction mixture containing the alcohol-substituted colorant, the solvent, and the anhydride is heated for any desirable or effective period of time, in one embodiment at least about 2.5 hours, and in another embodiment at least about 3 hours, and in one embodiment no more than about 5 hours, although the heating time can be outside of these ranges. Reaction completion can be determined by thin layer chromatography of the reaction mixture to detect the presence of unreacted reactants.

[0106] The ester-substituted colorant can be brominated to form a brominated ester-substituted colorant and its salt of the formulae

[0107] wherein Y is a hydrogen atom or a bromine atom and n is 1, 2, 3, or 4. A reaction mixture is prepared by admixing (1) the ester-substituted colorant, (2) bromine, and (3) a solvent, followed by quenching the reaction mixture with water to form a mixture of a brominated ester-substituted colorant and its salt, as follows (illustrated for an embodiment wherein the ester-substituted colorant is substituted with the ester group in the 4- or para-position and wherein the resulting brominated ester-substituted colorant has Y=hydrogen and 2 bromine atoms in the ortho positions adjacent to the nitrogen atom):

[0108] The mixture of products contains both an amine compound and the HBr salt thereof. When it is desired to brominate an alcohol-substituted colorant of the present invention, it can be desirable in some instances to convert the alcohol-substituted colorant to the ester-substituted colorant, followed by bromination of the ester-substituted colorant and subsequent conversion of the brominated ester-substituted colorant to the brominated alcohol-substituted colorant, since the presence of the ester group protects the R₁-containing moiety from undergoing reaction with HBr that is generated in the bromination reaction.

[0109] Bromine (Br₂) can be provided by any desired or effective method, such as by adding elemental bromine, or by generating Br₂ in situ in the reaction mixture by the addition of a combination of a bromide salt and a bromate salt, as disclosed in, for example, Kirk-Othmer Encyclopedia of Chemical Technology, Vol. 4, 4th Edition, ISBN 0-471-52672-X, John Wiley & Sons, Inc. (New York 1992), the disclosure of which is totally incorporated herein by reference, or the like.

[0110] The ester-substituted colorant and the bromine are present in any desired or effective relative amounts, in one embodiment at least about 2 moles of Br₂ per every one mole of ester-substituted colorant, in another embodiment at least about 2.5 moles of Br₂ per every one mole of ester-substituted colorant, and in yet another embodiment at least about 3 moles of Br₂ per every one mole of ester-substituted colorant, and in one embodiment no more than about 4 moles of Br₂ per every one mole of ester-substituted colorant, in another embodiment no more than about 3.5 moles of Br₂ per every one mole of ester-substituted colorant, and in yet another embodiment no more than about 3.25 moles of Br₂ per every one mole of ester-substituted colorant, although the amount of bromine can be outside of these ranges. Higher amounts of bromine lead to higher degrees of substitution with bromine atoms. Greater amounts of bromine and/or higher reaction temperatures are selected when it is desired to place a bromine atom in the Y position.

[0111] Examples of suitable solvents include acetic acid, propionic acid, formic acid, butyric acid, dimethyl formamide, dimethyl sulfoxide, hexamethyl phosphorus triamide (HMPA), tetrahydrofuran, or the like, as well as mixtures thereof. The solvent is present in any desired or effective amount, in one embodiment at least about 25 grams of ester-substituted colorant per every one liter of solvent, and in another embodiment at least about 100 grams of ester-substituted colorant per every one liter of solvent, and in one embodiment no more than about 200 grams of ester-substituted colorant per every one liter of solvent, although the amount of solvent can be outside of these ranges.

[0112] In some instances, the esterification reaction between (1) the alcohol-substituted colorant, (2) a solvent, and (3) an anhydride to form the ester-substituted colorant is carried out immediately prior to the bromination reaction to convert the ester-substituted colorant to the brominated ester-substituted colorant. In this instance, the ester-substituted colorant need not be recovered from its reaction mixture; rather, the bromine can be added directly to this mixture upon completion of the esterification, and no additional solvent need be added.

[0113] The reaction mixture containing the ester-substituted colorant, the bromine, and the solvent generally can be initially heated to a temperature of about 30° C. to about 40° C. The reaction of the ester-substituted colorant and the bromine tends to be exothermic, and the reaction mixture is generally maintained at a desirable temperature by controlling the rate of addition of bromine as well as by any desired external source, such as a heating mantle or the like. The reaction mixture containing the ester-substituted colorant, the bromine, and the solvent is maintained any desirable or effective temperature, in one embodiment at least about 25° C., and in another embodiment at least about 50° C., and in one embodiment no more than about 100° C., and in another embodiment no more than about 60° C., although the temperature can be outside of these ranges.

[0114] The reaction between the ester-substituted colorant and the bromine is allowed to proceed for any desirable or effective period of time, in one embodiment at least about 5 hours, and in one embodiment no more than about 24 hours, although the reaction time can be outside of these ranges.

[0115] Subsequent to completion of the reaction, the reaction mixture containing the ester-substituted colorant, the bromine, and the solvent can be poured into water to quench the reaction. Any desired or effective amount of water can be used, in one embodiment at least about 1.5 times as much water by volume as the volume of the reaction mixture, in another embodiment at least about 2 times as much water by volume as the volume of the reaction mixture, in yet another embodiment at least about 2 times as much water by volume as the volume of the reaction mixture, and in still another embodiment at least about 3 times as much water by volume as the volume of the reaction mixture, although the amount of water can be outside of these ranges.

[0116] The mixture of the brominated ester-substituted colorant and its salt can be recovered from the reaction mixture as a solid by filtration, washed, and dried.

[0117] The unbrominated alcohol-substituted colorant can also be converted to a brominated alcohol-substituted colorant by this same process, as follows (illustrated for an embodiment wherein the alcohol-substituted colorant is substituted with the ester group in the 4- or para-position and wherein the brominated alcohol-substituted colorant has Y=hydrogen and 2 bromine atoms in the ortho positions adjacent to the nitrogen atom):

[0118] A brominated alcohol-substituted colorant of the present invention of the formula

[0119] can be prepared by admixing (1) a mixture of the brominated ester-substituted colorant and its salt, (2) a base, (3) water, and (4) a solvent and heating the reaction mixture thus formed to form a brominated alcohol-substituted colorant (and also to convert any of the ammonium salt form of the brominated ester-substituted colorant to the amine form), as follows (illustrated for an embodiment wherein the brominated ester-substituted colorant is substituted with the ester group in the 4- or para-position and wherein the brominated ester-substituted colorant has Y=hydrogen and 2 bromine atoms in the ortho positions adjacent to the nitrogen atom):

[0120] The brominated ester-substituted colorant and its salt are added to a solvent, such as N-methylpyrrolidinone, dimethyl sulfoxide, dimethyl formamide, or the like, as well as mixtures thereof, in any desired or effective amount, in one embodiment about 1 gram of brominated ester-substituted colorant plus salt thereof per every 4 grams of solvent, although the amount of solvent can be higher or lower than this value.

[0121] Any desired or effective base can be used. Examples of suitable bases include sodium hydroxide, potassium hydroxide, and the like, as well as mixtures thereof. The base is present in any desired or effective amount, in one embodiment at least about 1 mole of base per mole of (brominated ester-substituted colorant plus salt thereof), in another embodiment at least about 1.5 moles of base per mole of (brominated ester-substituted colorant plus salt thereof), and in yet another embodiment at least about 2 moles of base per mole of (brominated ester-substituted colorant plus salt thereof), and in one embodiment no more than about 5 moles of base per mole of (brominated ester-substituted colorant plus salt thereof), and in another embodiment no more than about 3 moles of base per mole of (brominated ester-substituted colorant plus salt thereof), although the amount of base can be outside of these ranges.

[0122] The water is present in any desired or effective amount. The amount of water added can depend on the solvent used. Addition of too much water can cause precipitation of the ester before it is hydrolyzed. Hydrolysis can be accomplished with as little as a mole of water for every mole of ester. Some water is generated in situ by the neutralization of the HBr salt by the base. In one embodiment, the water is added with the base, as a (for example) 50 percent aqueous solution of the base; for example, when the base is NaOH, every mole of NaOH comes with 2.2 moles of water, so that the addition of 1 mole of base is accompanied by the addition of 2.2 moles of water, the addition of 1.5 moles of base is accompanied by the addition of 3.3 moles of water, the addition of 3 moles of base is accompanied by the addition of 6.6 moles of water, the addition of 5 moles of base is accompanied by the addition of 11.1 moles of water, and the like.

[0123] The reaction mixture containing the mixture of the brominated ester-substituted colorant and its salt, the base, the water, and the solvent is heated to any desirable or effective temperature, in one embodiment at least about 50° C., and in another embodiment at least about 60° C., and in one embodiment no more than about 70° C., and in another embodiment no more than about 60° C., although the temperature can be outside of these ranges.

[0124] The reaction mixture containing the mixture of the brominated ester-substituted colorant and its salt, the base, the water, and the solvent is heated for any desirable or effective period of time, in one embodiment at least about 45 minutes, and in one embodiment no more than about 90 minutes, although the heating time can be outside of these ranges.

[0125] Subsequent to completion of the reaction, the reaction mixture can be quenched by pouring it into water or by pouring water into the reaction mixture. Any desired or effective amount of water can be used, in one embodiment at least about 3 times as much water by volume as the volume of the reaction mixture, in another embodiment at least about 5 times as much water by volume as the volume of the reaction mixture, in yet another embodiment at least about 10 times as much water by volume as the volume of the reaction mixture, and in still another embodiment at least about 20 times as much water by volume as the volume of the reaction mixture, although the amount of water can be outside of these ranges.

[0126] The pH of the quenched reaction mixture can then be adjusted by addition of an acid, such as acetic acid, hydrochloric acid, hydrobromic acid, sulfuric acid, or the like, as well as mixtures thereof, until the desired pH is reached, in one embodiment at least about 5, and in another embodiment at least about 7, and in one embodiment no more than about 8, although the pH can be outside of these ranges.

[0127] The brominated alcohol-substituted colorant can be recovered from the quenched reaction mixture as a solid by filtration, followed by washing and drying.

[0128] The brominated alcohol-substituted colorant can be converted to a brominated ester-substituted colorant of the formula

[0129] wherein R₂′ is different from R₂ by admixing (1) the brominated alcohol-substituted colorant, (2) an esterification compound such as a carboxylic acid of the formula R₂COOH, wherein R₂ is as defined hereinabove, (3) a solvent, and (4) an optional esterification catalyst and heating the reaction mixture, as follows (illustrated for an embodiment wherein the brominated alcohol-substituted colorant is substituted with the ester group in the 4- or para-position and wherein the brominated ester-substituted colorant has Y=hydrogen and 2 bromine atoms in the ortho positions adjacent to the nitrogen atom):

[0130] The brominated alcohol-substituted colorant and the carboxylic acid are present in any desired or effective relative amounts, in one embodiment at least about 0.9 mole of carboxylic acid per every one mole of brominated alcohol-substituted colorant, in another embodiment at least about 0.95 mole of carboxylic acid per mole of brominated alcohol-substituted colorant, and in yet another embodiment at least about 1 mole of carboxylic acid per mole of brominated alcohol-substituted colorant, and in one embodiment no more than about 2 moles of carboxylic acid per mole of brominated alcohol-substituted colorant, in another embodiment no more than about 1.05 moles of carboxylic acid per mole of brominated alcohol-substituted colorant, and in yet another embodiment no more than about 1 mole of carboxylic acid per mole of brominated alcohol-substituted colorant, although the relative amounts of carboxylic acid and brominated alcohol-substituted colorant can be outside of these ranges.

[0131] When the optional esterification catalyst is present, any desired or effective esterification catalyst can be used, such as para-toluene sulfonic acid, dibutyl tin dilaurate, or the like, as well as mixtures thereof. The esterification catalyst is present in any desired or effective amount, in one embodiment at least about 0.05 mole of esterification catalyst per every one mole of brominated alcohol-substituted colorant, and in one embodiment no more than about 0.5 mole of esterification catalyst per mole of brominated alcohol-substituted colorant, although the amount of esterification catalyst can be outside of these ranges.

[0132] Any desired or effective solvent can be used. Examples of suitable solvents include xylene, toluene, benzene, chlorobenzene, nitrobenzene, dichlorobenzene, and the like, as well as mixtures thereof. The reactants are present in the solvent in any desired or effective amount, in one embodiment at least about 25 grams of brominated alcohol-substituted colorant per every one liter of solvent, in another embodiment at least about 50 grams of brominated alcohol-substituted colorant per every one liter of solvent, and in yet another embodiment at least about 100 grams of brominated alcohol-substituted colorant per everyone liter of solvent, and in one embodiment no more than about 200 grams of brominated alcohol-substituted colorant per every one liter of solvent, in another embodiment no more than about 150 grams of brominated alcohol-substituted colorant per every one liter of solvent, and in yet another embodiment no more than about 100 grams of brominated alcohol-substituted colorant per every one liter of solvent, although the amount of solvent can be outside of these ranges.

[0133] The reaction mixture containing the brominated alcohol-substituted colorant, the carboxylic acid, the solvent, and the optional esterification catalyst is heated to any desirable or effective temperature, typically the reflux temperature of the selected solvent, in one embodiment at least about 100° C., and in one embodiment no more than about 130° C., although the temperature can be outside of these ranges.

[0134] The reaction mixture containing the brominated alcohol-substituted colorant, the carboxylic acid, the solvent, and the optional esterification catalyst is heated for any desirable or effective period of time, in one embodiment at least about 2 hours, in another embodiment at least about 24 hours, and in one embodiment no more than about 72 hours, and in another embodiment no more than about 48 hours, although the heating time can be outside of these ranges.

[0135] The colorant of the formula

[0136] can be recovered from the reaction mixture as a solid by filtration, followed by washing and drying. If desired, purification can be carried out by filtration, redissolution in the solvent, heating, cooling, precipitating the colorant from the solution, filtering, washing the colorant with a solvent such as methanol, ethanol, or the like, and repeating this cycle until thin layer chromatography of the collected solid indicates that there is no detectable unreacted reactant present in the solid.

[0137] The unbrominated alcohol-substituted colorant can also be converted to an unbrominated ester-substituted colorant by this same process, as follows (illustrated for an embodiment wherein the alcohol-substituted colorant is substituted with the ester group in the 4- or para-position):

[0138] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, and R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group can be prepared by a process which comprises preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0139] followed by brominating and esterifying the alcohol-substituted colorant thus prepared, wherein either esterification can take place before bromination or bromination can take place before esterification.

[0140] In one specific embodiment, brominated ester-substituted colorants according to the present invention of the formula

[0141] can be prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0142] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) a solvent, and (3) an anhydride of the formula

[0143] wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group and heating the second reaction mixture to form a first ester-substituted colorant of the formula

[0144] (c) forming a third reaction mixture by admixing (1) the first ester-substituted colorant, (2) bromine, and (3) a solvent followed by

[0145] quenching the third reaction mixture with water to form a brominated ester-substituted colorant and a salt thereof, of the formulae

[0146] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 1, 2, 3, or 4; (d) preparing a fourth reaction mixture by admixing (1) the brominated ester-substituted colorant and the salt thereof, (2) a base, (3) water, and (4) a solvent and heating the fourth reaction mixture to form a brominated alcohol-substituted colorant of the formula

[0147] and (e) preparing a fifth reaction mixture by admixing (1) the brominated alcohol-substituted colorant, (2) a carboxylic acid of the formula R₂′COOH, wherein R₂′ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, and wherein R₂′ is different from R₂, (3) an optional esterification catalyst, and (4) a solvent and heating the fifth reaction mixture to form a second ester-substituted colorant of the formula

[0148] This process is particularly suitable for preparation of colorants wherein R₂ has 4 or fewer carbon atoms and wherein R₂′ has more than 4 carbon atoms.

[0149] Brominated ester-substituted colorants according to the present invention of the formula

[0150] can also be prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0151] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) a carboxylic acid of the formula R₂COOH, wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (3) an optional esterification catalyst, and (4) a solvent and heating the second reaction mixture to form an ester-substituted colorant of the formula

[0152] and (c) forming a third reaction mixture by admixing (1) the ester-substituted colorant, (2) bromine, and (3) a solvent followed by quenching the third reaction mixture with water to form a brominated ester-substituted colorant and a salt thereof, of the formulae

[0153] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 1, 2, 3, or 4.

[0154] Brominated ester-substituted colorants according to the present invention of the formula

[0155] can also be prepared by a process which comprises (a) preparing a first reaction mixture by admixing (1) leucoquinizarin and, optionally, quinizarin, (2) an aminobenzene substituted with an alcohol group of the formula —R₁—OH, wherein R₁ is an alkylene group or an arylalkylene group, (3) boric acid, and (4) an optional solvent, and heating the first reaction mixture to prepare an alcohol-substituted colorant of the formula

[0156] (b) preparing a second reaction mixture by admixing (1) the alcohol-substituted colorant, (2) bromine, and (3) a solvent followed by quenching the second reaction mixture with water to form a brominated alcohol-substituted colorant and a salt thereof, of the formulae

[0157] wherein Y is a hydrogen atom or a bromine atom and n is an integer of 0, 1, 2, 3, or 4; and (c) forming a third reaction mixture by admixing (1) the brominated alcohol-substituted colorant, (2) a carboxylic acid of the formula R₂COOH, wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (3) an optional esterification catalyst, and (4) a solvent and heating the third reaction mixture to form a brominated ester-substituted colorant of the formula

[0158] One disadvantage of running the bromination on the unprotected alcohol is that from about 10 to about 20 percent of the alcohol can be converted by the evolved HBr to the alkylbromide derivative; this derivative generally is not believed to be convertd to the desired ester in the next step of the synthesis and generally is removed by recrystallization. Nevertheless, in some embodiments, bromination of the unprotected alcohol can also be desirable.

[0159] Urethane-substituted colorants according to the present invention of the formula

[0160] can be prepared by any desired or effective method. One specific method entails the reaction of either an alcohol-substituted colorant according to the present invention of the formula

[0161] or a brominated alcohol-substituted colorant according to the present invention of the formula

[0162] with an isocyanate. Isocyanates react with alcohols to form urethanes. For example, a monoisocyanate reacts with an alcohol to form a urethane as follows:

[0163] wherein R_(a) and R_(b) each, independently of the other, is an alkyl group (including linear, branched, saturated, unsaturated, cyclic, unsubstituted, and substituted alkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the alkyl group), typically with from about 5 to about 100 carbon atoms, although the number of carbon atoms can be outside of this range, an aryl group (including unsubstituted and substituted aryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in the aryl group), typically with from about 5 to about 20 carbon atoms, although the number of carbon atoms can be outside of this range, an arylalkyl group (including unsubstituted and substituted arylalkyl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the arylalkyl group), typically with from about 6 to about 50 carbon atoms, although the number of carbon atoms can be outside of this range, or an alkylaryl group (including unsubstituted and substituted alkylaryl groups, and wherein hetero atoms, such as oxygen, nitrogen, sulfur, silicon, phosphorus, and the like either may or may not be present in either or both of the alkyl portion and the aryl portion of the alkylaryl group), typically with from about 6 to about 50 carbon atoms, although the number of carbon atoms can be outside of this range, and wherein the substituents on the substituted alkyl, alkylene, aryl, arylene, arylalkyl, arylalkylene, alkylaryl, and alkylarylene groups can be (but are not limited to) hydroxy groups, halogen atoms, amine groups, imine groups, ammonium groups, cyano groups, pyridine groups, pyridinium groups, ether groups, aldehyde groups, ketone groups, ester groups, amide groups, carbonyl groups, thiocarbonyl groups, sulfate groups, sulfonate groups, sulfide groups, sulfoxide groups, phosphine groups, phosphonium groups, phosphate groups, nitrile groups, mercapto groups, nitro groups, nitroso groups, sulfone groups, acyl groups, acid anhydride groups, azide groups, azo groups, cyanato groups, isocyanato groups, thiocyanato groups, isothiocyanato groups, mixtures thereof, and the like, wherein two or more substituents can be joined together to form a ring. Diisocyanates react similarly; for example, isophorone diisocyanate reacts with two moles of alcohol to form a diurethane as follows:

[0164] Examples of suitable isocyanates include monoisocyanates, diisocyanates, triisocyanates, copolymers of a diisocyanate, copolymers of a triisocyanate, polyisocyanates (having more than three isocyanate functional groups), and the like, as well as mixtures thereof. Examples of monoisocyanates include octadecylisocyanate; hexadecylisocyanate; octylisocyanate; butyl and t-butylisocyanate; cyclohexyl isocyanate; adamantyl isocyanate; ethylisocyanatoacetate; ethoxycarbonylisocyanate; phenylisocyanate; alphamethylbenzyl isocyanate; 2-phenylcyclopropyl isocyanate; benzylisocyanate; 2-ethylphenylisocyanate; benzoylisocyanate; meta and para-tolylisocyanate; 2-, 3-, or 4-nitrophenylisocyanates; 2-ethoxyphenyl isocyanate; 3-methoxyphenyl isocyanate; 4-methoxyphenylisocyanate; ethyl 4-isocyanatobenzoate; 2,6-dimethylphenylisocyante; 1-naphthylisocyanate; (naphthyl)ethylisocyantes; and the like, as well as mixtures thereof. Examples of diisocyanates include isophorone diisocyanate (IPDI); toluene diisocyanate (TDI); diphenylmethane-4,4′-diisocyanate (MDI); hydrogenated diphenylmethane-4,4′-diisocyanate (H12MDI); tetra-methyl xylene diisocyanate (TMXDI); hexamethylene-1,6-diisocyanate (HDI); hexamethylene-1,6-diisocyanate; napthylene-1,5-diisocyanate; 3,3′-dimethoxy-4,4′-biphenyldiisocyanate; 3,3′-dimethyl-4,4′-bimethyl-4,4′-biphenyldiisocyanate; phenylene diisocyanate; 4,4′-biphenydiiisocyanate; trimethylhexamethylene diisocyanate; tetramethylene xylene diisocyanate; 4,4′-methylenebis(2,6-diethylphenyl isocyanate); 1,12-diisocyanatododecane; 1,5-diisocyanato-2-methylpentane; 1,4-diisocyanatobutane; dimer diisocyanate and cyclohexylene diisocyanate and its isomers; uretidione dimers of HDI; and the like, as well as mixtures thereof. Examples of triisocyanates or their equivalents include the trimethylolpropane trimer of TDI, and the like, isocyanurate trimers of TDI, HDI, IPDI, and the like, and biuret trimers of TDI, HDI, IPDI, and the like, as well as mixtures thereof. Examples of higher isocyanate functionalities include copolymers of TDI/HDI, and the like, and MDI oligomers, as well as mixtures thereof.

[0165] Any suitable reaction condition for making urethane compounds by condensing alcohol's with isocyanates can be used to prepare urethane-substituted colorants according to the present invention. Typically (although not necessarily), the reaction is carried out at elevated temperatures (for example, from about 60 to about 160° C.) in the presence of an optional urethane reaction catalyst, such as dibutyl tindilaurate, bismuth tris-neodecanoate, cobalt benzoate, lithium acetate, stannous octoate, triethylamine, or the like. In a specific embodiment, the reaction conditions are conducted in an inert atmosphere, such as argon or nitrogen gas or other suitable gases, to prevent oxidizing or yellowing of the reaction products and to prevent undesirable side reactions. The reaction can employ an inert solvent, such as toluene or the like, or can be performed neat (i.e., without a solvent). The mole ratio of reactants is adjusted so that the isocyanate functionalities are completely consumed in the reaction with a slight molar excess of alcohol-substituted colorant typically remaining. The reactants can be added together in any order and/or added to the reaction as physical mixtures. If desired, reaction conditions and the order of the addition of reactants can be controlled for several reasons, such as to provide a controlled exothermic reaction, to tailor the distribution of molecules in the antioxidant-containing material, or the like. When doing these adjustments, the different reactivities to isocyanates of alcohols versus amines can be employed, as well as the different reactivities of the two separate isocyanate groups on IPDI. See, for example, J. H. Saunders and K. C. Frisch's “Polyurethanes Part I, Chemistry” published by Interscience of New York, N.Y. in 1962 and Olin Chemicals' LUXATE® IM isophorone diisocyanate technical product information sheet, which provide further explanation of this chemistry.

[0166] Phase change inks of the present invention contain a phase change carrier system or composition. The phase change carrier composition is typically designed for use in either a direct printing mode or an indirect or offset printing transfer system.

[0167] In the direct printing mode, the phase change carrier composition in one embodiment contains one or more materials that enable the phase change ink (1) to be applied in a thin film of uniform thickness on the final recording substrate (such as paper, transparency material, and the like) when cooled to ambient temperature after printing directly to the recording substrate, (2) to be ductile while retaining sufficient flexibility so that the applied image on the substrate will not fracture upon bending, and (3) to possess a high degree of lightness, chroma, transparency, and thermal stability.

[0168] In an offset printing transfer or indirect printing mode, the phase change carrier composition in one embodiment exhibits not only the characteristics desirable for direct printing mode inks, but also certain fluidic and mechanical properties desirable for use in such a system, as described in, for example, U.S. Pat. No. 5,389,958 the disclosure of which is totally incorporated herein by reference.

[0169] Any desired or effective carrier composition can be used. Examples of suitable ink carrier materials include fatty amides, such as monoamides, tetra-amides, mixtures thereof, and the like. Specific examples of suitable fatty amide ink carrier materials include stearyl stearamide, a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and stearic acid, a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and a carboxylic acid having at least about 36 carbon atoms, and the like, as well as mixtures thereof. When the fatty amide ink carrier is a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and a carboxylic acid having at least about 36 carbon atoms, the carboxylic acid is of the general formula

[0170] wherein R is an alkyl group, including linear, branched, saturated, unsaturated, and cyclic alkyl groups, said alkyl group in one embodiment having at least about 36 carbon atoms, in another embodiment having at least about 40 carbon atoms, said alkyl group in one embodiment having no more than about 200 carbon atoms, in another embodiment having no more than about 150 carbon atoms, and in yet another embodiment having no more than about 100 carbon atoms, although the number of carbon atoms can be outside of these ranges. Carboxylic acids of this formula are commercially available from, for example, Baker Petrolite, Tulsa, Okla., and can also be prepared as described in Example 1 of U.S. Pat. No. 6,174,937, the disclosure of which is totally incorporated herein by reference. Further information on fatty amide carrier materials is disclosed in, for example, U.S. Pat. No. 4,889,560, U.S. Pat. No. 4,889,761, U.S. Pat. No. 5,194,638, U.S. Pat. No. 4,830,671, U.S. Pat. No. 6,174,937, U.S. Pat. No. 5,372,852, U.S. Pat. No. 5,597,856, U.S. Pat. No. 6,174,937, and British Patent GB 2 238 792, the disclosures of each of which are totally incorporated herein by reference.

[0171] Also suitable as phase change ink carrier materials are isocyanate-derived resins and waxes, such as urethane isocyanate-derived materials, urea isocyanate-derived materials, urethane/urea isocyanate-derived materials, mixtures thereof, and the like. Further information on isocyanate-derived carrier materials is disclosed in, for example, U.S. Pat. No. 5,750,604, U.S. Pat. No. 5,780,528, U.S. Pat. No. 5,782,966, U.S. Pat. No. 5,783,658, U.S. Pat. No. 5,827,918, U.S. Pat. No. 5,830,942, U.S. Pat. No. 5,919,839, U.S. Pat. No. 6,255,432, U.S. Pat. No. 6,309,453, British Patent GB 2 294 939, British Patent GB 2 305 928, British Patent GB 2 305 670, British Patent GB 2 290 793, PCT Publication WO 94/14902, PCT Publication WO 97/12003, PCT Publication WO 97/13816, PCT Publication WO 96/14364, PCT Publication WO 97/33943, and PCT Publication WO 95/04760, the disclosures of each of which are totally incorporated herein by reference.

[0172] Mixtures of fatty amide materials and isocyanate-derived materials can also be employed as the ink carrier composition for inks of the present invention.

[0173] Additional suitable phase change ink carrier materials for the present invention include paraffins, microcrystalline waxes, polyethylene waxes, ester waxes, amide waxes, fatty acids, fatty alcohols, fatty amides and other waxy materials, sulfonamide materials, resinous materials made from different natural sources (such as, for example, tall oil rosins and rosin esters), and many synthetic resins, oligomers, polymers and copolymers, such as ethylene/vinyl acetate copolymers, ethylene/acrylic acid copolymers, ethylene/vinyl acetate/acrylic acid copolymers, copolymers of acrylic acid with polyamides, and the like, ionomers, and the like, as well as mixtures thereof. One or more of these materials can also be employed in a mixture with a fatty amide material and/or an isocyanate-derived material.

[0174] In one specific embodiment, the phase change ink carrier comprises (a) a polyethylene wax, present in the ink in an amount in one embodiment of at least about 25 percent by weight of the ink, in another embodiment of at least about 30 percent by weight of the ink, and in yet another embodiment of at least about 37 percent by weight of the ink, and in one embodiment of no more than about 60 percent by weight of the ink, in another embodiment of no more than about 53 percent by weight of the ink, and in yet another embodiment of no more than about 48 percent by weight of the ink, although the amount can be outside of these ranges; (b) a stearyl stearamide wax, present in the ink in an amount in one embodiment of at least about 8 percent by weight of the ink, in another embodiment of at least about 10 percent by weight of the ink, and in yet another embodiment of at least about 12 percent by weight of the ink, and in one embodiment of no more than about 32 percent by weight of the ink, in another embodiment of no more than about 28 percent by weight of the ink, and in yet another embodiment of no more than about 25 percent by weight of the ink, although the amount can be outside of these ranges; (c) a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and a long chain hydrocarbon having greater than thirty six carbon atoms and having a terminal carboxylic acid group, present in the ink in an amount in one embodiment of at least about 10 percent by weight of the ink, in another embodiment of at least about 13 percent by weight of the ink, and in yet another embodiment of at least about 16 percent by weight of the ink, and in one embodiment of no more than about 32 percent by weight of the ink, in another embodiment of no more than about 27 percent by weight of the ink, and in yet another embodiment of no more than about 22 percent by weight of the ink, although the amount can be outside of these ranges; (d) a urethane resin derived from the reaction of two equivalents of hydroabietyl alcohol and one equivalent of isophorone diisocyanate, present in the ink in an amount in one embodiment of at least about 6 percent by weight of the ink, in another embodiment of at least about 8 percent by weight of the ink, and in yet another embodiment of at least about 10 percent by weight of the ink, and in one embodiment of no more than about 16 percent by weight of the ink, in another embodiment of no more than about 14 percent by weight of the ink, and in yet another embodiment of no more than about 12 percent by weight of the ink, although the amount can be outside of these ranges; (e) a urethane resin that is the adduct of three equivalents of stearyl isocyanate and a glycerol-based alcohol, present in the ink in an amount in one embodiment of at least about 2 percent by weight of the ink, in another embodiment of at least about 3 percent by weight of the ink, and in yet another embodiment of at least about 4.5 percent by weight of the ink, and in one embodiment of no more than about 13 percent by weight of the ink, in another embodiment of no more than about 10 percent by weight of the ink, and in yet another embodiment of no more than about 7.5 percent by weight of the ink, although the amount can be outside of these ranges; and (f) an antioxidant, present in the ink in an amount in one embodiment of at least about 0.01 percent by weight of the ink, in another embodiment of at least about 0.05 percent by weight of the ink, and in yet another embodiment of at least about 0.1 percent by weight of the ink, and in one embodiment of no more than about 1 percent by weight of the ink, in another embodiment of no more than about 0.5 percent by weight of the ink, and in yet another embodiment of no more than about 0.3 percent by weight of the ink, although the amount can be outside of these ranges.

[0175] The ink carrier is present in the phase change ink of the present invention in any desired or effective amount, in one embodiment of at least about 0.1 percent by weight of the ink, in another embodiment of at least about 50 percent by weight of the ink, and in yet another embodiment of at least about 90 percent by weight of the ink, and in one embodiment of no more than about 99 percent by weight of the ink, in another embodiment of no more than about 98 percent by weight of the ink, and in yet another embodiment of no more than about 95 percent by weight of the ink, although the amount can be outside of these ranges.

[0176] The phase change inks of the present invention contain a colorant compound of the formula

[0177] wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, and X is (a) a hydrogen atom, (b) a group of the formula

[0178] wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (c) an alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, or (d) a group of the formula

[0179] wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group. This colorant is present in the ink in any desired or effective amount to obtain the desired color or hue, in one embodiment of at least about 1 percent by weight of the ink, in another embodiment of at least about 2 percent by weight of the ink, and in yet another embodiment of at least about 3 percent by weight of the ink, and in one embodiment of no more than about 20 percent by weight of the ink, in another embodiment of no more than about 13 percent by weight of the ink, and in yet another embodiment of no more than about 6 percent by weight of the ink, although the amount can be outside of these ranges. The colorant according to the present invention can either be the sole colorant in the ink or can be present in combination with other colorants, such as dyes, pigments, mixtures thereof, and the like.

[0180] In a specific embodiment, the inks of the present invention include a xanthene dye in addition to the colorant according to the present invention. Suitable xanthene dyes include rhodamine dyes and the like. One particularly preferred rhodamine dye is C.I. Solvent Red 49. The xanthene dye can be present in the inks of the present invention in any desired or effective amount to achieve the desired color, hue, and other characteristics. In specific embodiments, when a xanthene dye is present, the inks of the present invention further contain an organic sulfonic acid. Specific examples of organic sulfonic acids include alkyl benzene sulfonic acids such as para-toluene-sulfonic acid, dodecylbenzenesulfonic acid, and the like, as well as mixtures thereof. The organic sulfonic acid is present in any desired or effective amount, in one embodiment at least about 2 percent by weight of the amount of xanthene dye, and in another embodiment at least about 5 percent by weight of the amount of xanthene dye, and in one embodiment no more than about 100 percent by weight of the amount of the xanthene dye, and in another embodiment no more than about 30 percent by weight of the xanthene dye, although the amount of organic sulfonic acid can be outside of these ranges.

[0181] The inks of the present invention can also optionally contain an antioxidant. The optional antioxidants of the ink compositions protect the images from oxidation and also protect the ink components from oxidation during the heating portion of the ink preparation process. Specific examples of suitable antioxidants include NAUGUARD® 524, NAUGUARD® 76, and NAUGUARD® 512, commercially available from Uniroyal Chemical Company, Oxford, Conn., IRGANOX® 1010, commercially available from Ciba Geigy, and the like. When present, the optional antioxidant is present in the ink in any desired or effective amount, in one embodiment of at least about 0.01 percent by weight of the ink, in another embodiment of at least about 0.1 percent by weight of the ink, and in yet another embodiment of at least about 1 percent by weight of the ink, and in one embodiment of no more than about 20 percent by weight of the ink, in another embodiment of no more than about 5 percent by weight of the ink, and in yet another embodiment of no more than about 3 percent by weight of the ink, although the amount can be outside of these ranges.

[0182] The inks of the present invention can also optionally contain a viscosity modifier. Examples of suitable viscosity modifiers include aliphatic ketones, such as stearone, and the like. When present, the optional viscosity modifier is present in the ink in any desired or effective amount, in one embodiment of at least about 0.1 percent by weight of the ink, in another embodiment of at least about 1 percent by weight of the ink, and in yet another embodiment of at least about 10 percent by weight of the ink, and in one embodiment of no more than about 99 percent by weight of the ink, in another embodiment of no more than about 30 percent by weight of the ink, and in yet another embodiment of no more than about 15 percent by weight of the ink, although the amount can be outside of these ranges.

[0183] Other optional additives to the inks include clarifiers, such as UNION CAMP® X37-523-235 (commercially available from Union Camp), in an amount in one embodiment of at least about 0.01 percent by weight of the ink, in another embodiment of at least about 0.1 percent by weight of the ink, and in yet another embodiment of at least about 5 percent by weight of the ink, and in one embodiment of no more than about 98 percent by weight of the ink, in another embodiment of no more than about 50 percent by weight of the ink, and in yet another embodiment of no more than about 10 percent by weight of the ink, although the amount can be outside of these ranges, tackifiers, such as FORAL® 85, a glycerol ester of hydrogenated abietic (rosin) acid (commercially available from Hercules), FORAL® 105, a pentaerythritol ester of hydroabietic (rosin) acid (commercially available from Hercules), CELLOLYN® 21, a hydroabietic (rosin) alcohol ester of phthalic acid (commercially available from Hercules), ARAKAWA KE-311 Resin, a triglyceride of hydrogenated abietic (rosin) acid (commercially available from Arakawa Chemical Industries, Ltd.), synthetic polyterpene resins such as NEVTAC® 2300, NEVTAC® 100, and NEVTAC® 80 (commercially available from Neville Chemical Company), WINGTACK® 86, a modified synthetic polyterpene resin (commercially available from Goodyear), and the like, in an amount in one embodiment of at least about 0.1 percent by weight of the ink, in another embodiment of at least about 5 percent by weight of the ink, and in yet another embodiment of at least about 10 percent by weight of the ink, and in one embodiment of no more than about 98 percent by weight of the ink, in another embodiment of no more than about 75 percent by weight of the ink, and in yet another embodiment of no more than about 50 percent by weight of the ink, although the amount can be outside of these range, adhesives, such as VERSAMID® 757, 759, or 744 (commercially available from Henkel), in an amount in one embodiment of at least about 0.1 percent by weight of the ink, in another embodiment of at least about 1 percent by weight of the ink, and in yet another embodiment of at least about 5 percent by weight of the ink, and in one embodiment of no more than about 98 percent by weight of the ink, in another embodiment of no more than about 50 percent by weight of the ink, and in yet another embodiment of no more than about 10 percent by weight of the ink, although the amount can be outside of these ranges, plasticizers, such as UNIPLEX® 250 (commercially available from Uniplex), the phthalate ester plasticizers commercially available from Monsanto under the trade name SANTICIZER®, such as dioctyl phthalate, diundecyl phthalate, alkylbenzyl phthalate (SANTICIZER® 278), triphenyl phosphate (commercially available from Monsanto), KP-140®, a tributoxyethyl phosphate (commercially available from FMC Corporation), MORFLEX® 150, a dicyclohexyl phthalate (commercially available from Morflex Chemical Company Inc.), trioctyl trimellitate (commercially available from Eastman Kodak Co.), and the like, in an amount in one embodiment of at least about 0.1 percent by weight of the ink, in another embodiment of at least about 1 percent by weight of the ink, and in yet another embodiment of at least about 2 percent by weight of the ink, and in one embodiment of no more than about 50 percent by weight of the ink, in another embodiment of no more than about 30 percent by weight of the ink, and in yet another embodiment of no more than about 10 percent by weight of the ink, although the amount can be outside of these ranges, and the like.

[0184] The ink compositions of the present invention in one embodiment have melting points of no lower than about 50° C., in another embodiment of no lower than about 70° C., and in yet another embodiment of no lower than about 80° C., and have melting points in one embodiment of no higher than about 160° C., in another embodiment of no higher than about 140° C., and in yet another embodiment of no higher than about 100° C., although the melting point can be outside of these ranges.

[0185] The ink compositions of the present invention generally have melt viscosities at the jetting temperature (in one embodiment no lower than about 75° C., in another embodiment no lower than about 100° C., and in yet another embodiment no lower than about 120° C., and in one embodiment no higher than about 180° C., and in another embodiment no higher than about 150° C., although the jetting temperature can be outside of these ranges) in one embodiment of no more than about 30 centipoise, in another embodiment of no more than about 20 centipoise, and in yet another embodiment of no more than about 15 centipoise, and in one embodiment of no less than about 2 centipoise, in another embodiment of no less than about 5 centipoise, and in yet another embodiment of no less than about 7 centipoise, although the melt viscosity can be outside of these ranges.

[0186] The ink compositions of the present invention can be prepared by any desired or suitable method. For example, the ink ingredients can be mixed together, followed by heating, to a temperature in one embodiment of at least about 100° C., and in one embodiment of no more than about 140° C., although the temperature can be outside of these ranges, and stirring until a homogeneous ink composition is obtained, followed by cooling the ink to ambient temperature (typically from about 20 to about 25° C.). The inks of the present invention are solid at ambient temperature. In a specific embodiment, during the formation process, the inks in their molten state are poured into molds and then allowed to cool and solidify to form ink sticks.

[0187] The inks of the present invention can be employed in apparatus for direct printing ink jet processes and in indirect (offset) printing ink jet applications. Another embodiment of the present invention is directed to a process which comprises incorporating an ink of the present invention into an ink jet printing apparatus, melting the ink, and causing droplets of the melted ink to be ejected in an imagewise pattern onto a recording substrate. A direct printing process is also disclosed in, for example, U.S. Pat. No. 5,195,430, the disclosure of which is totally incorporated herein by reference. Yet another embodiment of the present invention is directed to a process which comprises incorporating an ink of the present invention into an ink jet printing apparatus, melting the ink, causing droplets of the melted ink to be ejected in an imagewise pattern onto an intermediate transfer member, and transferring the ink in the imagewise pattern from the intermediate transfer member to a final recording substrate. An offset or indirect printing process is also disclosed in, for example, U.S. Pat. No. 5,389,958, the disclosure of which is totally incorporated herein by reference. In one specific embodiment, the printing apparatus employs a piezoelectric printing process wherein droplets of the ink are caused to be ejected in imagewise pattern by oscillations of piezoelectric vibrating elements. Inks of the present invention can also be employed in other hot melt printing processes, such as hot melt acoustic ink jet printing, hot melt thermal ink jet printing, hot melt continuous stream or deflection ink jet printing, and the like. Phase change inks of the present invention can also be used in printing processes other than hot melt ink jet printing processes.

[0188] Any suitable substrate or recording sheet can be employed, including plain papers such as XEROX® 4024 papers, XEROX® Image Series papers, Courtland 4024 DP paper, ruled notebook paper, bond paper, silica coated papers such as Sharp Company silica coated paper, JuJo paper, Hammermill Laserprint Paper, and the like, transparency materials, fabrics, textile products, plastics, polymeric films, inorganic substrates such as metals and wood, and the like.

[0189] Specific embodiments of the invention will now be described in detail. These examples are intended to be illustrative, and the invention is not limited to the materials, conditions, or process parameters set forth in these embodiments. All parts and percentages are by weight unless otherwise indicated.

EXAMPLE I Part A

[0190] In a glass reaction flask were combined 73 grams of sublimed quinizarin (obtained from Aceto Corp., Lake Success, N.Y.), 49 grams of leucoquinizarin (obtained from Aceto Corp.), 66 grams of 4-aminobenzene ethanol (obtained from Aceto Corp.), 31 grams of boric acid (obtained from Aldrich Chemical Co., Milwaukee, Wis.), and 780 grams of methanol (obtained from JT Baker, Phillipsburg, N.J.). The materials were mixed and heated until the solvent refluxed at about 66° C.

[0191] After about 16 hours of reflux the reaction was complete, having generated an alcohol-substituted colorant of the formula

[0192] The reaction mixture was cooled and filtered. The product filter cake was dried in air at ambient temperature.

[0193] The spectral strength of the alcohol-substituted colorant was determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the alcohol-substituted colorant was measured as about 21,000 mL Absorbance Units per gram at absorption λ_(max), indicating a purity of about 80 percent.

Part B-1

[0194] In a glass reaction flask were combined 8 grams of the alcohol-substituted colorant prepared in Part A of this Example, 68 grams of glacial acetic acid (obtained from JT Baker), 13 grams of propionic acid (obtained from Aldrich Chemical Co.), and 2.3 grams of acetic anhydride (obtained from Aldrich Chemical Co.). The materials were mixed and heated to a reflux temperature of about 121° C. After about 4 hours of reflux, the reaction was complete and the reaction mixture contained an ethyl acetate-substituted colorant of the formula

Part B-2

[0195] In a glass reaction flask were combined 12 grams of the alcohol-substituted colorant prepared in Part A of this Example, 10.2 grams of dimer diisocyanate (obtained from Cognis; these materials are also described in, for example, Kirk-Othmer Encyclopedia of Chemical Technology 1979, volume 7, 3^(rd) edition, p. 768-782, John Wiley and Sons, Inc., the disclosure of which is totally incorporated herein by reference), and 1 drop of FASCAT 4202 catalyst (obtained from Atofina). The materials were mixed and heated to a temperature of about 120° C. After about 1 hour of heating, the reaction mixture became very thick, so the temperature was raised to about 150° C. and stirred for 4 hours. IR analysis showed that the reaction was complete (no isocyanate peak) and the reaction mixture contained a dimer-diurethane-substituted colorant of the formula

[0196] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

Part B-3

[0197] In a glass reaction flask fitted with a Dean-Stark trap were combined 5 grams of the alcohol-substituted colorant prepared in Part A of this Example, 60 grams of xylenes (obtained from Aldrich Chemical Co.), 8.4 grams of the Guerbet acid 2-hexadecyl-1-eicosanoic acid (ISOCARB 36, obtained from Condea Vista, Austin, Tex.), and 0.25 grams of p-toluene sulfonic acid (obtained from Boliden Intertrade). The materials were mixed and heated to a reflux in an oil bath at 150° C. After about 19 hours of reflux, the reaction was complete and the reaction mixture contained an ISOCARB-36-ester substituted colorant of the formula

Part B-4

[0198] In a glass reaction flask fitted with a Dean-Stark trap were combined 15 grams of the alcohol-substituted colorant prepared in Part A of this Example, 200 grams of xylenes (obtained from Aldrich Chemical Co.), 14.3 grams dimer acid hydrogenated (known as PRIPOL 1006, obtained from Unichema International; these materials are also described in, for example, Kirk-Othmer Encyclopedia of Chemical Technology 1979, volume 7, 3^(rd) edition, p. 768-782, John Wiley and Sons, Inc., the disclosure of which is totally incorporated herein by reference), and 0.5 grams of p-toluene sulfonic acid (obtained from Boliden Intertrade). The materials were mixed and heated to a reflux in an oil bath at 150° C. After about 19 hours of reflux, the reaction was complete and the reaction mixture contained a dimer acid di-substituted colorant of the formula

[0199] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

Part B-5

[0200] In a glass reaction flask were combined 3.0 grams of the alcohol-substituted colorant prepared in Part A of this Example and 6.4 grams of hydroabietyl alcohol (obtained as Abitol E from Hercules Inc., Wilmington Del.). The mixture was heated to a temperature of about 140° C. until it was homogeneous. 1 drop of FASCAT 4202 catalyst (obtained from Atofina) and 3.2 grams of isophorone diisocyanate (DESMODUR I, obtained from Bayer Corp., Pittsburgh, Pa.) were then added and the materials were mixed and heated to a temperature of about 140° C. After about 5 hours of heating, IR analysis showed that the reaction was complete (no isocyanate peak) and the reaction mixture contained a diurethane-substituted colorant of the formula

Part C-1

[0201] About 91 grams of the reaction mixture containing the ethyl acetate-substituted colorant from Part B-1 of this Example was charged into a glass reaction flask. The mixture was cooled to a minimum of 30° C. While mixing, about 9 grams of bromine (obtained from Aldrich Chemical Co.) was added to the mixture at a rate such that the temperature remained below about 40° C. The mixture was then heated to about 40° C. After about 24 hours of mixing the reaction was complete.

[0202] The reaction mixture was then quenched into 234 grams of deionized water and allowed to cool to room temperature. The reaction mixture was then filtered. The filter cake was reslurried and filtered twice in deionized water to remove most of the residual acetic acid. The filter cake was then dried in a 60° C. oven. This filter cake contained a mixture of brominated ethyl acetate-substituted colorants of the formulae

[0203] The spectral strength of the brominated ethyl acetate-substituted colorant was determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the brominated ethyl acetate-substituted colorant was measured as about 15,000 mL Absorbance Units per gram at absorption λ_(max). This spectral strength indicated a purity of about 60 percent.

Part C-2

[0204] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-2 of this Example. It is believed that a colorant of the formulae

[0205] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formulae

[0206] will be obtained.

Part C-3

[0207] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-3 of this Example. It is believed that a colorant of the formulae

[0208] will be obtained.

Part C-4

[0209] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-4 of this Example. It is believed that a colorant of the formulae

[0210] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

[0211] will be obtained.

Part C-5

[0212] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-5 of this Example. It is believed that a colorant of the formulae

[0213] will be obtained.

Part D

[0214] In a glass reaction flask were combined 18 grams of the mixture of the brominated ethyl acetate-substituted colorant and its salt prepared in Part C-1 of this Example, 72 grams of N-methyl-2-pyrrolidone (obtained from Aldrich Chemical Co.), 4 grams of sodium hydroxide (obtained from Aldrich Chemical Co.), and 4 grams of deionized water. The materials were mixed and heated to about 60° C. After about 3 hours the reaction was complete.

[0215] The reaction mixture was then quenched into 234 grams of deionized water and allowed to cool to room temperature. Glacial acetic acid was added until the solution reached a pH of between 6 and 7. The reaction mixture was then filtered. The filter cake was reslurried and filtered twice in deionized water to remove most of the residual N-methyl-2-pyrrolidone. The filter cake was then dried in a 60° C. oven. This filter cake contained a brominated alcohol-substituted colorant of the formula

[0216] The spectral strength of the brominated alcohol-substituted colorant was determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in an equal mixture of toluene and tetrahydrofuran and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the brominated alcohol-substituted colorant was measured as about 16,000 mL Absorbance Units per gram at absorption λ_(max). This spectral strength indicated a purity of about 60 percent.

Part E

[0217] In a glass reaction flask were combined 16 grams of the brominated alcohol-substituted colorant prepared in Part D of this Example, 31 grams of UNICID® 700 (a material containing carboxylic acid of the formula R₂COOH wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms, also containing other unfunctionalized wax materials in an amount of up to about 25 percent by weight; obtained from Baker Petrolite, Sugarland, Tex.), 152 grams of xylene (obtained from Tarr, Inc., Portland, Oreg.), and 0.6 grams of para-toluenesulfonic acid (obtained from Capital Resin Corp., Columbus, Ohio). The materials were mixed and heated to a reflux temperature of about 143° C. After about 7 hours, the reaction was complete.

[0218] The reaction mixture was then cooled to 40° C. and filtered. The filter cake was reslurried and filtered two more times in methanol to remove residual xylene. The filter cake was then dried in air at ambient temperature. This filter cake contained a colorant of the formula

[0219] wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms.

[0220] The spectral strength of the colorant was determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in an equal mixture of toluene and tetrahydrofuran and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the colorant was measured as about 5,000 mL Absorbance Units per gram at absorption λ_(max). This spectral strength indicated a purity of about 40 percent.

Part F

[0221] Compounds of the formulae shown in Parts C-1 through C-5 of this Example are prepared by reversing steps B and C of this Example. More specifically, the alcohol-substituted colorant prepared in Part A of this Example is first subjected to bromination as described in Parts C-1 through C-5 of this Example, and the resulting brominated alcohol-substituted colorants are then subjected to esterification as described in Parts C-1 through C-5 of this Example.

EXAMPLE II Part A

[0222] In a glass reaction flask are combined 73 grams of sublimed quinizarin (available from Aceto Corp., Lake Success, N.Y.), 49 grams of leucoquinizarin (available from Aceto Corp.), 66 grams of 3-aminobenzene ethanol (available from Frinton Labs, Vineland, N.J.), 31 grams of boric acid (available from Aldrich Chemical Co., Milwaukee, Wis.), and 780 grams of methanol (available from JT Baker, Phillipsburg, N.J.). The materials are mixed and heated until the solvent refluxes at about 66° C. After about 16 hours of reflux, it is believed that the reaction will be complete, having generated an alcohol-substituted colorant of the formula

[0223] The reaction mixture is cooled and filtered. The product filter cake is dried in air at ambient temperature. The spectral strength of the alcohol-substituted colorant is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the alcohol-substituted colorant is believed to be measured as about 21,000 mL Absorbance Units per gram at absorption λ_(max).

Part B-1

[0224] In a glass reaction flask are combined 8 grams of the alcohol-substituted colorant prepared in Part A of this Example, 68 grams of glacial acetic acid (available from JT Baker), 13 grams of propionic acid (available from Aldrich Chemical Co.), and 2.3 grams of acetic anhydride (available from Aldrich Chemical Co.). The materials are mixed and heated to a reflux temperature of about 121° C. After about 4 hours of reflux, the reaction is complete and the reaction mixture contains an ethyl acetate-substituted colorant of the formula

Part B-2

[0225] In a glass reaction flask are combined 12 grams of the alcohol-substituted colorant prepared in Part A of this Example, 10.2 grams of dimer diisocyanate (available from Cognis; these materials are also described in, for example, Kirk-Othmer Encyclopedia of Chemical Technology 1979, volume 7, 3^(rd) edition, p. 768-782, John Wiley and Sons, Inc., the disclosure of which is totally incorporated herein by reference), and 1 drop of FASCAT 4202 catalyst (available from Atofina). The materials are mixed and heated to a temperature of about 120° C. After about 1 hour of heating, the reaction mixture becomes very thick, so the temperature is raised to about 150° C. and stirred for 4 hours. It is believed that IR analysis will show that the reaction is complete (no isocyanate peak), and that the reaction mixture will contain a dimer-diurethane-substituted colorant of the formula

[0226] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

Part B-3

[0227] In a glass reaction flask fitted with a Dean-Stark trap are combined 5 grams of the alcohol-substituted colorant prepared in Part A of this Example, 60 grams of xylenes (available from Aldrich Chemical Co.), 8.4 grams of the Guerbet acid 2-hexadecyl-1-eicosanoic acid (ISOCARB 36, available from Condea Vista, Austin, Tex.), and 0.25 grams of p-toluene sulfonic acid (available from Boliden Intertrade). The materials are mixed and heated to a reflux in an oil bath at 150° C. After about 19 hours of reflux, it is believed that the reaction will be complete and that the reaction mixture will contain an ISOCARB-36-ester substituted colorant of the formula

Part B-4

[0228] In a glass reaction flask fitted with a Dean-Stark trap are combined 15 grams of the alcohol-substituted colorant prepared in Part A of this Example, 200 grams of xylenes (available from Aldrich Chemical Co.), 14.3 grams of dimer acid hydrogenated (known as PRIPOL 1006, available from Unichema International; these materials are also described in, for example, Kirk-Othmer Encyclopedia of Chemical Technology 1979, volume 7, 3^(rd) edition, p. 768-782, John Wiley and Sons, Inc., the disclosure of which is totally incorporated herein by reference), and 0.5 grams of p-toluene sulfonic acid (available from Boliden Intertrade). The materials are mixed and heated to a reflux in an oil bath at 150° C. After about 19 hours of reflux, it is believed that the reaction will be complete and that the reaction mixture will contain a dimer acid di-ester substituted colorant of the formula

[0229] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

Part B-5

[0230] In a glass reaction flask are combined 3.0 grams of the alcohol-substituted colorant prepared in Part A of this Example and 6.4 grams of hydroabietyl alcohol (available as Abitol E from Hercules Inc., Wilmington, Del.) and the mixture is heated to a temperature of about 140° C. until it is homogeneous. 1 drop of FASCAT 4202 catalyst (available from Atofina) and 3.2 grams of isophorone diisocyanate (available as DESMODUR I from Bayer Corp., Pittsburgh, Pa.) are then added and the materials are mixed and heated to a temperature of about 140° C. After about 5 hours of heating, it is believed that IR analysis will show that the reaction is complete (no isocyanate peak) and that the reaction mixture will contain a diurethane-substituted colorant of the formula

Part C-1

[0231] About 91 grams of the reaction mixture containing the ethyl acetate-substituted colorant from Part B-1 of this Example is charged into a glass reaction flask. The mixture is cooled to a minimum of 30° C. While mixing, about 9 grams of bromine (available from Aldrich Chemical Co.) is added to the mixture at a rate such that the temperature remains below about 40° C. The mixture is then heated to about 40° C. After about 24 hours of mixing, the reaction is complete. The reaction mixture is then quenched into 234 grams of deionized water, allowed to cool to room temperature, and filtered. The filter cake is reslurried and filtered twice in deionized water to remove most of the residual acetic acid. The filter cake is then dried in a 60° C. oven. It is believed that this filter cake will contain a mixture of brominated ethyl acetate-substituted colorants of the formulae

[0232] The spectral strength of the brominated ethyl acetate-substituted colorant is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. It is believed that the spectral strength of the alcohol-substituted colorant will be measured as about 21,000 mL Absorbance Units per gram at absorption λ_(max).

Part C-2

[0233] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-2 of this Example. It is believed that a colorant of the formulae

[0234] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formulae

[0235] will be obtained.

Part C-3

[0236] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-3 of this Example. It is believed that a colorant of the formulae

[0237] will be obtained.

Part C-4

[0238] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-4 of this Example. It is believed that a colorant of the formulae

[0239] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

[0240] and

[0241] will be obtained.

Part C-5

[0242] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-5 of this Example. It is believed that a colorant of the formulae

[0243] will be obtained.

Part D

[0244] In a glass reaction flask are combined 18 grams of the mixture of the brominated ethyl acetate-substituted colorant and its salt prepared in Part C-1 of this Example, 72 grams of N-methyl-2-pyrrolidone (available from Aldrich Chemical Co.), 4 grams of sodium hydroxide (available from Aldrich Chemical Co.), and 4 grams of deionized water. The material is mixed and heated to about 60° C. After about 3 hours the reaction is complete. The reaction mixture is then quenched into 234 grams of deionized water and allowed to cool to room temperature. Glacial acetic acid is added until the solution reaches a pH of between 6 and 7. The reaction mixture is then filtered. The filter cake is reslurried and filtered twice in deionized water to remove most of the residual N-methyl-2-pyrrolidone. The filter cake is then dried in a 60° C. oven. It is believed that this filter cake will contain a brominated alcohol-substituted colorant of the formula

[0245] The spectral strength of the brominated alcohol-substituted colorant can be determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in an equal mixture of toluene and tetrahydrofuran and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. It is believed that the spectral strength of the brominated alcohol-substituted colorant will be measured as about 16,000 mL Absorbance Units per gram at absorption λ_(max), which would indicate a purity of about 60 percent.

Part E

[0246] In a glass reaction flask are combined 16 grams of the brominated alcohol-substituted colorant prepared in Part D of this Example, 31 grams of UNICID® 700 (a material containing carboxylic acids of the formula R₂COOH wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms, also containing other unfunctionalized wax materials in an amount of up to about 25 percent by weight; available from Baker Petrolite, Sugarland, Tex.), 152 grams of xylene (available from Tarr, Inc., Portland, Oreg.), and 0.6 grams of para-toluenesulfonic acid (available from Capital Resin Corp., Columbus, Ohio). The materials are mixed and heated to a reflux temperature of about 143° C. After about 7 hours, the reaction is complete. The reaction mixture is then cooled to 40° C. and filtered. The filter cake is reslurried and filtered two more times in methanol to remove residual xylene. The filter cake is then dried in air at ambient temperature. It is believed that this filter cake will contain a colorant of the formula

[0247] wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms.

[0248] The spectral strength of the colorant can be determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in an equal mixture of toluene and tetrahydrofuran and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. It is believed that the spectral strength of the colorant will be measured as about 5,000 mL Absorbance Units per gram at absorption λ_(max), which would indicate a purity of about 40 percent.

Part F

[0249] Compounds of the formulae shown in Parts C-1 through C-5 of this Example are prepared by reversing steps B and C of this Example. More specifically, the alcohol-substituted colorant prepared in Part A of this Example is first subjected to bromination as described in Parts C-1 through C-5 of this Example, and the resulting brominated alcohol-substituted colorants are then subjected to esterification as described in Parts C-1 through C-5 of this Example.

EXAMPLE III Part A

[0250] In a glass reaction flask are combined 73 grams of sublimed-quinizarin (available from Aceto Corp., Lake Success, N.Y.), 49 grams of leucoquinizarin (available from Aceto Corp.), 95.8 grams of 4-(4-hydroxybenzyl)aniline (which can be prepared as outlined in scheme 3 of de Groot et al., J. Org. Chemistry 2001, 66(26), p 8815-8830, the disclosure of which is totally incorporated herein by reference), 31 grams of boric acid (available from Aldrich Chemical Co., Milwaukee, Wis.), and 780 grams of isopropyl alcohol (available from JT Baker, Phillipsburg, N.J.). The materials are mixed and heated until the solvent refluxes at about 75° C. After about 16 hours of reflux it is believed that the reaction will be complete, having generated an alcohol-substituted colorant of the formula

[0251] The reaction mixture is cooled and filtered. The product filter cake is dried in air at ambient temperature. The spectral strength of the alcohol-substituted colorant can be determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer.

Part B-I

[0252] In a glass reaction flask are combined 9.4 grams of the alcohol-substituted colorant prepared in Part A of this Example, 68 grams of glacial acetic acid (available from JT Baker), 13 grams of propionic acid (available from Aldrich Chemical Co.), and 2.3 grams of acetic anhydride (available from Aldrich Chemical Co.). The materials are mixed and heated to a reflux temperature of about 121° C. After about 4 hours of reflux, the reaction is complete and it is believed that the reaction mixture will contain an ethyl acetate-substituted colorant of the formula

Part B-2

[0253] In a glass reaction flask are combined 14.1 grams of the alcohol-substituted colorant prepared in Part A of this Example, 10.2 grams of dimer diisocyanate (available from Cognis; these materials are also described in, for example, Kirk-Othmer Encyclopedia of Chemical Technology 1979, volume 7, 3^(rd) edition, p. 768-782, John Wiley and Sons, Inc., the disclosure of which is totally incorporated herein by reference), and 1 drop of FASCAT 4202 catalyst (available from Atofina). The materials are mixed and heated to a temperature of about 150° C. and stirred for 4 hours. It is believed that IR analysis will show that the reaction is complete (no isocyanate peak) and that the reaction mixture will contain a dimer-diurethane-substituted colorant of the formula

[0254] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

Part B-3

[0255] In a glass reaction flask fitted with a Dean-Stark trap are combined 5.9 grams of the alcohol-substituted colorant prepared in Part A of this Example, 60 grams of xylenes (available from Aldrich Chemical Co.), 8.4 grams of the Guerbet acid 2-hexadecyl-1-eicosanoic acid (ISOCARB 36, available from Condea Vista, Austin, Tex.), and 0.25 grams of p-toluene sulfonic acid (available from Boliden Intertrade). The materials are mixed and heated to reflux in an oil bath at 150° C. After about 19 hours of reflux, the reaction is complete and it is believed that the reaction mixture will contain an ISOCARB-36-substituted colorant of the formula

Part B-4

[0256] In a glass reaction flask fitted with a Dean-Stark trap are combined 17.6 grams of the alcohol-substituted colorant prepared in Part A of this Example, 200 grams of xylenes (available from Aldrich Chemical Co.), 14.3 grams of dimer acid hydrogenated (known as PRIPOL 1006, available from Unichema International; these materials are also described in, for example, Kirk-Othmer Encyclopedia of Chemical Technology 1979, volume 7, 3^(rd) edition, p. 768-782, John Wiley and Sons, Inc., the disclosure of which is totally incorporated herein by reference), and 0.5 grams of p-toluene sulfonic acid (available from Boliden Intertrade). The material is mixed and heated to reflux in an oil bath at 150° C. After about 19 hours of reflux, it is believed that the reaction will be complete and that the reaction mixture will contain a dimer acid di-ester substituted colorant of the formula

[0257] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

Part B-5

[0258] In a glass reaction flask are combined 3.5 grams of the alcohol-substituted colorant prepared in Part A of this Example and 6.4 grams of hydroabietyl alcohol (available as Abitol E from Hercules Inc. of Wilmington Del.) and the mixture is heated to a temperature of about 140° C. until it is homogeneous. 1 drop of FASCAT 4202 catalyst (available from Atofina) and 3.2 grams of isophorone diisocyanate (available as DESMODUR I from Bayer Corp., Pittsburgh, Pa.) are added. The materials are mixed and heated to a temperature of about 140° C. After about 5 hours of heating it is believed that IR analysis will show that the reaction is complete (no isocyanate peak) and that the reaction mixture will contain a diurethane-substituted colorant of the formula

Part C-1

[0259] About 107 grams of the reaction mixture containing the ethyl acetate-substituted colorant from Part B-1 of this Example is charged into a glass reaction flask. The mixture is cooled to a minimum of 30° C. While mixing, about 9 grams of bromine (available from Aldrich Chemical Co.) is added to the mixture at a rate such that the temperature remaines below about 40° C. The mixture is then heated to about 40° C. After about 24 hours of mixing the reaction is complete. The reaction mixture is then quenched into 234 grams of deionized water and allowed to cool to room temperature. The reaction mixture is then filtered and the filter cake is reslurried and filtered twice in deionized water to remove most of the residual acetic acid. The filter cake is then dried in a 60° C. oven. It is believed that this filter cake will contain a mixture of brominated ethyl acetate-substituted colorants of the formulae

[0260] The spectral strength of the brominated ethyl acetate-substituted colorant can be determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer.

Part C-2

[0261] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-2 of this Example. It is believed that a colorant of the formulae

[0262] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formulae

[0263] will be obtained.

Part C-3

[0264] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-3 of this Example. It is believed that a colorant of the formulae

[0265] will be obtained.

Part C-4

[0266] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-4 of this Example. It is believed that a colorant of the formulae

[0267] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formulae

[0268] will be obtained.

Part C-5

[0269] The process of Part C-1 of this Example is repeated except that the colorant from Part B-1 of this Example is replaced with the colorant from Part B-5 of this Example. It is believed that a colorant of the formulae

[0270] will be obtained.

Part D

[0271] In a glass reaction flask are combined 18 grams of the mixture of the brominated ethyl acetate-substituted colorant and its salt prepared in Part C-1 of this Example, 72 grams of N-methyl-2-pyrrolidone (available from Aldrich Chemical Co.), 4 grams of sodium hydroxide (available from Aldrich Chemical Co.), and 4 grams of deionized water. The material is mixed and heated to about 60° C. After about 3 hours the reaction is complete. The reaction mixture is then quenched into 234 grams of deionized water and allowed to cool to room temperature. Glacial acetic acid is added until the solution reaches a pH of between 6 and 7. The reaction mixture is then filtered and the filter cake is reslurried and filtered twice in deionized water to remove most of the residual N-methyl-2-pyrrolidone. The filter cake is then dried in a 60° C. oven. It is believed that this filter cake will contain a brominated alcohol-substituted colorant of the formula

[0272] The spectral strength of the brominated alcohol-substituted colorant can be determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in an equal mixture of toluene and tetrahydrofuran and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer.

Part E

[0273] In a glass reaction flask are combined 18.8 grams of the brominated alcohol-substituted colorant prepared in Part D of this Example, 31 grams of UNICID® 700 (a material containing carboxylic acids of the formula R₂COOH wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms, also containing other unfunctionalized wax materials in an amount of up to about 25 percent by weight; obtained from Baker Petrolite, Sugarland, Tex.), 152 grams of xylene (obtained from Tarr, Inc., Portland, Oreg.), and 0.6 grams of para-toluenesulfonic acid (obtained from Capital Resin Corp., Columbus, Ohio). The materials are mixed and heated to a reflux temperature of about 143° C. After about 7 hours, the reaction is complete. The reaction mixture is then cooled to 40° C. and filtered and the filter cake is reslurried and filtered two more times in methanol to remove residual xylene. The filter cake is then dried in air at ambient temperature. It is believed that this filter cake will contain a colorant of the formula

[0274] wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms.

Part F

[0275] Compounds of the formulae shown in Parts C-1 through C-5 of this Example are prepared by reversing steps B and C of this Example. More specifically, the alcohol-substituted colorant prepared in Part A of this Example is first subjected to bromination as described in Parts C-1 through C-5 of this Example, and the resulting brominated alcohol-substituted colorants are then subjected to esterification as described in Parts C-1 through C-5 of this Example.

EXAMPLE IV Part A

[0276] In a 500 milliliter round bottom flask equipped with magnetic stirrer were combined 24.6 grams of 3-(1-hydroxyethyl) aniline, of the formula

[0277] (obtained from Aldrich Chemical Co., Milwaukee, Wis.), 17.4 grams of leucoquinizarin (obtained from Aceto Corp., Lake Success, N.Y.), 25.9 grams of quinizarin (obtained from Aceto Corp.), 10.9 grams of boric acid (obtained from Aldrich Chemical Co.), and 275.5 grams of methanol. The flask was placed under stirring and a condenser in a hot oil bath at about 120° C. for 19 hours. Thereafter the reaction mixture was poured hot into a 1 liter beaker and allowed to cool in a refrigerator. Thereafter, precipitated solids were collected by vacuum filtration, rinsing, and washing with cold methanol. The collected solids were dried overnight in a vacuum oven at about 50° C. to yield 58.5 grams of the product, believed to be of the formula

Part B

[0278] In a glass reaction flask are combined 12 grams of the alcohol-substituted colorant prepared as described in Part A of this Example, 10.2 grams of dimer diisocyanate (available from Cognis), and 1 drop of FASCAT 4202 catalyst (available from Atofina). The materials are mixed and heated to a temperature of about 120° C. After about 1 hour of heating, the reaction mixture becomes very thick, so the temperature is raised to about 150° C. and the reaction mixture stirred for 4 hours. It is believed that at this point IR analysis will show that the reaction is complete (no isocyanate peak) and that the reaction mixture will contain a dimer-diurethane-substituted colorant of the formula

[0279] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formula

Part C

[0280] In a glass reaction flask are combined the dimer diurethane-substituted colorant prepared as described in Part B of this Example, 68 grams of glacial acetic acid (available from JT Baker), and 13 grams of propionic acid (available from Aldrich Chemical Co). The mixture is cooled to a minimum of 30° C. While mixing, about 6.1 grams of bromine (available from Aldrich Chemical Co.) are added to the mixture at a rate such that the temperature remains below about 40° C. The mixture is then heated to about 40° C. After about 24 hours of mixing the reaction is complete. The reaction mixture is then quenched into about 250 grams of deionized water, allowed to cool to room temperature, and filtered. The product is reslurried and filtered twice in deionized water to remove most of the residual acetic acid. The product is then dried in a 60° C. oven. It is believed that this product will contain a mixture of brominated ethyl acetate-substituted colorants of the formulae

[0281] wherein C₃₆H_(62+n) is a branched alkylene group which may include unsaturations and cyclic groups, wherein n is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10, one isomer of which is believed to be of the formulae

EXAMPLE V Part A

[0282] In a 100 milliliter glass reaction flask equipped with a magnet and a stirring oil bath at about 130° C. were combined 30 grams (representing a large excess) of fresh (unopened jar) benzaldehyde (obtained from Aldrich Chemical Co.), 10.7 grams of 4-aminobenzene ethanol (obtained from Aceto Corp.), and about 35 grams of butanol (obtained from JT Baker, Phillipsburg, N.J.). The materials were mixed and heated until the solvent refluxed and the mixture was then held at reflux.

[0283] After about 4 hours of reflux, a distillation column was attached and the excess benzaldehyde and the butanol were distilled off. To ensure that the benzaldehyde and the butanol were completely removed, a vacuum was applied and the temperature was held at about 130° C. for 1 hour. The reaction had generated a protected alcohol-substituted aniline of the formula

[0284] The benzaldehyde protected 4-aminobenzene ethanol was cooled to room temperature with a nitrogen gas blanket. The neat product was then dissolved in about 100 milliliters of HPLC grade acetonitrile and transferred to a 250 milliliter 1 neck roundbottom flask with magnet and a reflux condenser with a nitrogen blanket on the top of the condenser. About 3 milliliters of BF₃-etherate (available from the Aldrich Chemical Co., of the formula BF₃.CH₃—CH₂—O—CH₂—CH₃) was then added and 39.0 grams of propylene oxide (available from Adrich Chemical Co.) was added over 1 hour while keeping the reaction flask at room temperature. A hot water bath was then added and stirring continued. The resulting product, while not characterized, is believed to be a slightly viscous liquid of the formula

[0285] After heating for an hour, about 30 grams of 6 Molar hydrochloric acid is added to the reaction mixture and heating/stirring is continued for an additional hour. The acetonitrile, the liberated benzaldehyde, and the water (from the HCl) are then distilled off and the resultant liquid is believe to be of the formula:

Part B

[0286] In a glass reaction flask are combined 73 grams of sublimed quinizarin (available from Aceto Corp., Lake Success, N.Y.), 49 grams of eucoquinizarin (available from Aceto Corp.), 289 grams of propoxylated 4-aminobenzene ethanol (prepared as described in Part A of this Example), 31 grams of boric acid (available from Aldrich Chemical Co., Milwaukee, Wis.), and 780 grams of isopropanol (available from JT Baker, Phillipsburg, N.J.). The materials are mixed and heated until the solvent refluxes. After about 16 hours of reflux the reaction is complete, having generated an alcohol-substituted colorant of the formula

[0287] The reaction mixture is cooled and filtered and the product filter cake is dried in air at ambient temperature.

[0288] The spectral strength of the alcohol-substituted colorant can be determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the colorant in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer.

Part C

[0289] In a glass reaction flask are combined 18.3 grams of the alcohol-substituted colorant prepared in Part B of this Example, 68 grams of glacial acetic acid (available from JT Baker), 13 grams of propionic acid (available from Aldrich Chemical Co.), and 2.3 grams of acetic anhydride (available from Aldrich Chemical Co.). The materials are mixed and heated to a reflux temperature of about 121° C. After about 4 hours of reflux, the reaction is complete and it is believed that the reaction mixture will contain an ethyl acetate-substituted colorant of the formula

Part D

[0290] About 91 grams of the reaction mixture containing the acetylated colorant from Part C of this Example is charged into a glass reaction flask. The mixture is cooled to a minimum of 30° C. While mixing, about 8 grams of bromine (available from Aldrich Chemical Co.) is added to the mixture at a rate such that the temperature remains below about 40° C. The mixture is then heated to about 40° C. After about 24 hours of mixing, the reaction is complete. The reaction mixture is then quenched into 234 grams of deionized water and allowed to cool to room temperature. The liquid contains a mixture of brominated acetylated propoxylated-colorants of the formulae

Part E

[0291] In a glass reaction flask are combined 18 grams of the mixture of the aqueous brominated, acetylated, propoxylated colorant and its salt prepared in Part D of this Example and 4 grams of sodium hydroxide (available from Aldrich Chemical Co.). The materials are mixed and heated to about 60° C. After about 3 hours the reaction is complete. The reaction mixture is then allowed to cool to room temperature. Glacial acetic acid is added until the solution reaches a pH of between 6 and 7. The aqueous, neutralized reaction product is then heated with stirring to about 95° C. (above the cloud point of the product). It is then transferred to a separatory funnel and allowed to cool and separate. The salt water layer is removed and the product layer (still containing some water) is then transferred to a one neck round bottom flask and placed on a rotary evaporator. The water is then removed under vacuum. It is believed that the remaining viscous liquid will contain a brominated, propoxylated, alcohol-substituted colorant of the formulae

Part F

[0292] In a glass reaction flask are combined 12 grams of the brominated alcohol-substituted colorant prepared in Part E of this Example, 3.6 grams of octadecyl isocyanate (Mondur O, available from Bayer Corp), and 1 drop of FASCAT 4202 catalyst (available from Atofina). The materials are mixed and heated to a temperature of about 120° C. After about 4 hours of heating, it is believed that IR analysis will show that the reaction is complete (no isocyanate peak) and that the reaction mixture will contain an octadecyl urethane-substituted colorant of the formula

EXAMPLE VI

[0293] A phase change ink according to the present invention was prepared as follows. In a stainless steel beaker were combined 430 grams of polyethylene wax (PE 655, obtained from Baker Petrolite, Tulsa, Okla., of the formula CH₃(CH₂)₅₀CH₃), 194 grams of stearyl stearamide wax (KEMAMIDE® S-180, obtained from Crompton Corporation, Greenwich, Conn.), 219 grams of a tetra-amide resin obtained from the reaction of one equivalent of a C-36 dimer acid obtained from Uniqema, New Castle, Del. with two equivalents of ethylene diamine and UNICID® 700 (obtained from Baker Petrolite, Tulsa, Okla., a long chain hydrocarbon having a terminal carboxylic acid group), prepared as described in Example 1 of U.S. Pat. No. 6,174,937, the disclosure of which is totally incorporated herein by reference, 77 grams of a urethane resin obtained from the reaction of two equivalents of ABITOL® E hydroabietyl alcohol (obtained from Hercules Inc., Wilmington, Del.) and one equivalent of isophorone diisocyanate, prepared as described in Example 1 of U.S. Pat. No. 5,782,966, the disclosure of which is totally incorporated herein by reference, 46 grams of a urethane resin that was the adduct of three equivalents of stearyl isocyanate and a glycerol-based alcohol, prepared as described in Example 4 of U.S. Pat. No. 6,309,453, the disclosure of which is totally incorporated herein by reference, and 2.0 gram of NAUGUARD® 445 antioxidant (obtained from Uniroyal Chemical Co., Middlebury, Conn.). The materials were melted together at a temperature of about 140° C. in an oven, then blended by stirring in a temperature controlled mantle at about 135° C. for about 0.5 hour. To this mixture was then added about 20 grams of the magenta colorant prepared as described in Example I, Part E. In addition, about 4.6 grams of Solvent Red 49 dye (a rhodamine dye obtained from BASF, Germany) was added along with about 7.5 grams of dodecyl benzene sulfonic acid (BioSoft S-101, obtained from Steoan Company, Northfield, Ill.). After stirring for about 3 additional hours, the magenta ink thus formed was filtered through a heated MOTT® apparatus (obtained from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 pounds per square inch. The filtered phase change ink was poured into molds and allowed to solidify to form ink sticks.

[0294] The magenta phase change ink thus prepared exhibited a viscosity of about 10.6 centipoise as measured by a Rheometrics cone-plate viscometer at about 140° C., a melting point of about 80° C. as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, a glass transition temperature (T_(g)) of about 14° C., and a spectral strength, determined by using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in a 1:1 solution of tetrahydrofuran:toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer, of about 140 milliliters absorbance per gram at λ_(max) 535 nanometers.

[0295] The magenta ink thus prepared was placed in a XEROX® PHASER 860 printer, which uses a printing process wherein the ink is first jetted in an imagewise pattern onto an intermediate transfer member followed by transfer of the imagewise pattern from the intermediate transfer member to a final recording substrate. The ink was printed with a printhead temperature of 138° C. and an intermediate transfer drum temperature of 64° C. with HAMMERMILL LASERPRINT® paper (obtained from International Paper, Memphis, Tenn.).

[0296] A transmission spectrum for the phase change ink was evaluated on a commercially available spectrophotometer, the ACS SPECTRO-SENSOR II, in accordance with the measuring methods stipulated in ASTM 1E805 (Standard Practice of Instrumental Methods of Color or Color Difference Measurements of Materials) using the appropriate calibration standards supplied by the instrument manufacturer. For purposes of verifying and quantifying the overall calorimetric performance of the ink, measurement data were reduced, via tristimulus integration, following ASTM E308 (Standard Method for Computing the Colors of Objects using the CIE System) in order to calculate the 1976 CIE L* (Lightness), a* (redness-greenness), and b* (yellowness-blueness) CIELAB values for the phase change ink sample. In addition, the values for CIELAB Psychometric Chroma, C*_(ab), and CIELAB Psychometric Hue Angle, were calculated according to publication CIE15.2, Colorimetry (Second Edition, Central Bureau de la CIE, Vienna, 1986). The CIE L*a*b* color coordinates of printed swatches of the ink were as follows:

[0297] L*: 53

[0298] a*: 79

[0299] b*: −45

[0300] c*: 91

[0301] As is apparent to one skilled in the art, the CIE L*a*b* values represent an excellent magenta shade printed ink.

EXAMPLE VII

[0302] The process of Example VI is repeated except that the colorant prepared in Example II Part E is substituted for the colorant prepared in Example I Part E. It is believed that similar results will be obtained.

EXAMPLE VIII

[0303] The process of Example VI is repeated except that the colorant prepared in Example III Part E is substituted for the colorant prepared in Example I Part E. It is believed that similar results will be obtained.

EXAMPLE IX

[0304] Ink compositions are prepared by repeating the process of Example VI except instead of using the colorant prepared in Example I Part E, the colorants used are those prepared as described in Example I Part A, Example I Part B-1, Example I Part B-2, Example I Part B-3, Example I Part B-4, Example I Part B-5, Example I Part C-1, Example I Part C-2, Example I Part C-3, Example I Part C-4, Example I Part C-5, Example I Part D, Example II Part A, Example II Part B-1, Example II Part B-2, Example II Part B-3, Example II Part B-4, Example III Part B-5, Example II Part C-1, Example II Part C-2, Example II Part C-3, Example II Part C-4, Example II Part C-5, Example II Part D, Example III Part A, Example III Part B-1, Example III Part B-2, Example III Part B-3, Example III Part B-4, Example III Part B-5, Example III Part C-1, Example III Part C-2, Example III Part C-3, Example III Part C-4, Example III Part C-5, Example III Part D, Example IV Part A, Example IV Part B, Example IV Part C, Example V Part B, Example V Part C, Example V Part D, Example V Part E, and Example V Part F. The inks thus prepared are incorporated into an ink jet printing apparatus and printed by the method described in Example VI.

EXAMPLE X

[0305] A phase change ink according to the present invention is prepared as follows. A solid ink carrier composition is prepared as described in Example 11 of U.S. Pat. No. 5,780,528, the disclosure of which is totally incorporated herein by reference. To this composition is added about 2.0 percent by weight of the magenta compound prepared as described in Example I, Part E. In addition, about 0.5 weight percent of Solvent Red 49 dye (a rhodamine dye obtained from BASF, Germany) is added along with about 0.75 weight percent of dodecyl benzene sulfonic acid (BioSoft S-101, obtained from Stepan Company, Northfield, Ill.). After stirring for about 3 additional hours, the magenta ink thus formed is filtered through a heated MOTT® apparatus (obtained from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 pounds per square inch. The filtered phase change ink is poured into molds and is allowed to solidify to form ink sticks.

[0306] It is believed that the magenta phase change ink thus prepared will exhibit a viscosity of about 111 to 13 centipoise as measured by a Rheometrics cone-plate viscometer at about 140° C., a melting point of about 80° C. as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, a glass transition temperature (T_(g)) of about 14° C., and a spectral strength (determined by using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in toluene and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer) of about 150 milliliters absorbance per gram at about 555 nanometers.

EXAMPLE XI

[0307] The process of Example X is repeated except that the colorant prepared in Example II Part E is substituted for the colorant prepared in Example I Part E. It is believed that similar results will be obtained.

EXAMPLE XII

[0308] The process of Example X is repeated except that the colorant prepared in Example III Part E is substituted for the colorant prepared in Example I Part E. It is believed that similar results will be obtained.

EXAMPLE XIII

[0309] Ink compositions are prepared by repeating the process of Example X except instead of using the colorant prepared in Example I Part E, the colorants used are those prepared as described in Example I Part A, Example I Part B-1, Example I Part B-2, Example I Part B-3, Example I Part B-4, Example I Part B-5, Example I Part C-1, Example I Part C-2, Example I Part C-3, Example I Part C-4, Example I Part C-5, Example I Part D, Example II Part A, Example II Part B-1, Example II Part B-2, Example II Part B-3, Example II Part B-4, Example II Part B-5, Example II Part C-1, Example II Part C-2, Example II Part C-3, Example II Part C-4, Example II Part C-5, Example II Part D, Example III Part A, Example III Part B-1, Example III Part B-2, Example III Part B-3, Example III Part B-4, Example III Part B-5, Example III Part C-1, Example III Part C-2, Example III Part C-3, Example III Part C-4, Example III Part C-5, Example III Part D, Example IV Part A, Example IV Part B, Example IV Part C, Example V Part B, Example V Part C, Example V Part D, Example V Part E, and Example V Part F. The inks thus prepared are incorporated into an ink jet printing apparatus and printed by the method described in Example X.

[0310] Other embodiments and modifications of the present invention may occur to those of ordinary skill in the art subsequent to a review of the information presented herein; these embodiments and modifications, as well as equivalents thereof, are also included within the scope of this invention.

[0311] The recited order of processing elements or sequences, or the use of numbers, letters, or other designations therefor, is not intended to limit a claimed process to any order except as specified in the claim itself. 

What is claimed is:
 1. A phase change ink composition comprising a phase change ink carrier and a colorant compound of the formula

wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, and X is (a) a hydrogen atom, (b) a group of the formula

wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (c) an alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, or (d) a group of the formula

wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.
 2. A phase change ink composition according to claim 1 wherein the phase change ink carrier comprises a monoamide, a tetra-amide, or a mixture thereof.
 3. A phase change ink composition according to claim 1 wherein the phase change ink carrier comprises (a) stearyl stearamide, (b) a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and stearic acid, or (c) mixtures thereof.
 4. A phase change ink composition according to claim 1 wherein the phase change ink carrier comprises (a) stearyl stearamide, (b) a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and a carboxylic acid having at least about 36 carbon atoms, or (c) mixtures thereof.
 5. A phase change ink composition according to claim 4 wherein the carboxylic acid has at least about 40 carbon atoms, and wherein the carboxylic acid has no more than about 200 carbon atoms.
 6. A phase change ink composition according to claim 1 wherein the phase change ink carrier comprises an isocyanate-derived material.
 7. A phase change ink composition according to claim 1 wherein the phase change ink carrier comprises a urethane isocyanate-derived material, a urea isocyanate-derived material, a urethane/urea isocyanate-derived material, or mixtures thereof.
 8. A phase change ink composition according to claim 1 wherein the phase change ink carrier comprises a mixture of one or more amides and one or more isocyanate-derived materials.
 9. A phase change ink composition according to claim 1 wherein the phase change ink carrier comprises one or more materials selected from paraffins, microcrystalline waxes, polyethylene waxes, ester waxes, amide waxes, fatty acids, fatty alcohols, fatty amides, sulfonamide materials, tall oil rosins, rosin esters, ethylene/vinyl acetate copolymers, ethylene/acrylic acid copolymers, ethylene/vinyl acetate/acrylic acid copolymers, copolymers of acrylic acid with polyamides, ionomers, and mixtures thereof.
 10. A phase change ink composition according to claim 1 wherein the phase change ink carrier is present in the ink in an amount of at least about 0.1 percent by weight of the ink and wherein the phase change ink carrier is present in the ink in an amount of no more than about 99 percent by weight of the ink.
 11. A phase change ink composition according to claim 1 wherein the phase change ink carrier is present in the ink in an amount of at least about 50 percent by weight of the ink and wherein the phase change ink carrier is present in the ink in an amount of no more than about 98 percent by weight of the ink.
 12. A phase change ink composition according to claim 1 wherein the phase change ink carrier is present in the ink in an amount of at least about 90 percent by weight of the ink and wherein the phase change ink carrier is present in the ink in an amount of no more than about 95 percent by weight of the ink.
 13. A phase change ink composition according to claim 1 wherein the ink further contains an antioxidant.
 14. A phase change ink composition according to claim 13 wherein the antioxidant is present in the ink in an amount of at least about 0.01 percent by weight of the ink, and wherein the antioxidant is present in the ink in an amount of no more than about 20 percent by weight of the ink.
 15. A phase change ink composition according to claim 1 wherein the ink further contains a viscosity modifier.
 16. A phase change ink composition according to claim 15 wherein the viscosity modifier is an aliphatic ketone.
 17. A phase change ink composition according to claim 15 wherein the viscosity modifier is present in the ink in an amount of at least about 0.1 percent by weight of the ink and wherein the viscosity modifier is present in the ink in an amount of no more than about 99 percent by weight of the ink.
 18. A phase change ink composition according to claim 1 wherein the ink carrier comprises (a) a polyethylene wax, (b) a stearyl stearamide wax, (c) a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and a carboxylic acid having at least about 36 carbon atoms, (d) a urethane resin derived from the reaction of two equivalents of hydroabietyl alcohol and one equivalent of isophorone diisocyanate, (e) a urethane resin that is the adduct of three equivalents of stearyl isocyanate and a glycerol-based alcohol, and (f) an antioxidant.
 19. A phase change ink composition according to claim 1 wherein the ink carrier comprises (a) a polyethylene wax in an amount of at least about 25 percent by weight of the ink and in an amount of no more than about 60 percent by weight of the ink, (b) a stearyl stearamide wax in an amount of at least about 8 percent by weight of the ink and in an amount of no more than about 32 percent by weight of the ink, (c) a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and a carboxylic acid having at least about 36 carbon atoms in an amount of at least about 10 percent by weight of the ink and in an amount of no more than about 32 percent by weight of the ink, (d) a urethane resin derived from the reaction of two equivalents of hydroabietyl alcohol and one equivalent of isophorone diisocyanate in an amount of at least about 6 percent by weight of the ink and in an amount of no more than about 16 percent by weight of the ink, (e) a urethane resin that is the adduct of three equivalents of stearyl isocyanate and a glycerol-based alcohol in an amount of at least about 2 percent by weight of the ink and in an amount of no more than about 13 percent by weight of the ink, and (f) an antioxidant in an amount of at least about 0.01 percent by weight of the ink and in an amount of no more than about 1 percent by weight of the ink.
 20. A phase change ink composition according to claim 1 wherein the colorant is present in the ink in an amount of at least about 1 percent by weight of the ink.
 21. A phase change ink composition according to claim 1 wherein the colorant is present in the ink in an amount of at least about 2 percent by weight of the ink.
 22. A phase change ink composition according to claim 1 wherein the colorant is present in the ink in an amount of at least about 3 percent by weight of the ink.
 23. A phase change ink composition according to claim 1 wherein the colorant is present in the ink in an amount of no more than about 20 percent by weight of the ink.
 24. A phase change ink composition according to claim 1 wherein the colorant is present in the ink in an amount of no more than about 13 percent by weight of the ink.
 25. A phase change ink composition according to claim 1 wherein the colorant is present in the ink in an amount of no more than about 6 percent by weight of the ink.
 26. A phase change ink composition according to claim 1 wherein the ink has a melting point of no lower than about 50° C. and wherein the ink has a melting point of no higher than about 160° C.
 27. A phase change ink composition according to claim 1 wherein the ink has a melting point of no lower than about 70° C. and wherein the ink has a melting point of no higher than about 140° C.
 28. A phase change ink composition according to claim 1 wherein the ink has a melting point of no lower than about 80° C. and wherein the ink has a melting point of no higher than about 100° C.
 29. A phase change ink composition according to claim 1 wherein the ink has a melt viscosity at a temperature of about 140° C. of no more than about 30 centipoise.
 30. A phase change ink composition according to claim 1 herein the ink has a melt viscosity at a temperature of about 140° C. of no more than about 20 centipoise.
 31. A phase change ink composition according to claim 1 wherein the ink has a melt viscosity at a temperature of about 140° C. of no more than about 15 centipoise.
 32. A phase change ink composition according to claim 1 wherein the ink has a melt viscosity at a temperature of about 140° C. of no less than about 1 centipoise.
 33. A phase change ink composition according to claim 1 wherein the ink has a melt viscosity at a temperature of about 140° C. of no less than about 5 centipoise.
 34. A phase change ink composition according to claim 1 wherein the ink has a melt viscosity at a temperature of about 140° C. of no less than about 7 centipoise.
 35. A phase change ink composition according to claim 1 further containing a xanthene dye.
 36. A phase change ink composition according to claim 35 wherein the xanthene dye is a rhodamine dye.
 37. A phase change ink composition according to claim 36 wherein the rhodamine dye is Solvent Red
 49. 38. A phase change ink composition according to claim 35 further containing an organic sulfonic acid.
 39. A phase change ink composition according to claim 38 wherein the organic sulfonic acid is para-toluene-sulfonic acid, dodecylbenzenesulfonic acid, or a mixture thereof.
 40. A phase change ink composition according to claim 1 wherein Y is a hydrogen atom.
 41. A phase change ink composition according to claim 1 wherein n is
 0. 42. A phase change ink composition according to claim 1 wherein n is
 2. 43. A phase change ink composition according to claim 1 wherein the colorant is of the formula


44. A phase change ink composition according to claim 1 wherein the colorant is of the formula


45. A phase change ink composition according to claim 1 wherein the colorant is of the formula


46. A phase change ink composition according to claim 1 wherein the colorant is of the formula


47. A phase change ink composition according to claim 1 wherein R₁ is an unsubstituted alkylene group.
 48. A phase change ink composition according to claim 1 wherein R₁ is a substituted alkylene group.
 49. A phase change ink composition according to claim 1 wherein R₁ is an alkylene group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the alkylene group.
 50. A phase change ink composition according to claim 1 wherein R₁ is an alkylene group wherein no hetero atoms are present in the alkylene group.
 51. A phase change ink composition according to claim 1 wherein R₁ is an alkylene group having at least about 2 carbon atoms.
 52. A phase change ink composition according to claim 1 wherein R₁ is an unsubstituted arylalkylene group.
 53. A phase change ink composition according to claim 1 wherein R₁ is a substituted arylalkylene group.
 54. A phase change ink composition according to claim 1 wherein R₁ is an arylalkylene group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the arylalkylene group.
 55. A phase change ink composition according to claim 1 wherein R₁ is an arylalkylene group wherein no hetero atoms are present in the arylalkylene group.
 56. A phase change ink composition according to claim 1 wherein R₁ is of the formula


57. A phase change ink composition according to claim 1 wherein R₁ is of the formula


58. A phase change ink composition according to claim 1 wherein X is a hydrogen atom.
 59. A phase change ink composition according to claim 1 wherein X is a group of the formula

wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.
 60. A phase change ink composition according to claim 59 wherein R₂ is an unsubstituted alkyl group.
 61. A phase change ink composition according to claim 59 wherein R₂ is a substituted alkyl group.
 62. A phase change ink composition according to claim 59 wherein R₂ is an alkyl group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the alkyl group.
 63. A phase change ink composition according to claim 59 wherein R₂ is an alkyl group wherein no hetero atoms are present in the alkyl group.
 64. A phase change ink composition according to claim 59 wherein R₂ is an unsubstituted aryl group.
 65. A phase change ink composition according to claim 59 wherein R₂ is a substituted aryl group.
 66. A phase change ink composition according to claim 59 wherein R₂ is an aryl group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the aryl group.
 67. A phase change ink composition according to claim 59 wherein R₂ is an aryl group wherein no hetero atoms are present in the aryl group.
 68. A phase change ink composition according to claim 59 wherein R₂ is an unsubstituted arylalkyl group or an unsubstituted alkylaryl group.
 69. A phase change ink composition according to claim 59 wherein R₂ is a substituted arylalkyl group or a substituted alkylaryl group.
 70. A phase change ink composition according to claim 59 wherein R₂ is an arylalkyl group or an alkylaryl group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the arylalkyl group or alkylaryl group.
 71. A phase change ink composition according to claim 59 wherein R₂ is an arylalkyl group or an alkylaryl group wherein no hetero atoms are present in the arylalkyl group or alkylaryl group.
 72. A phase change ink composition according to claim 59 wherein R₂ is


73. A phase change ink composition according to claim 59 wherein R₂ is


74. A phase change ink composition according to claim 59 wherein R₂ is

wherein C₃₆H_(62+m) is a branched alkylene group which may include unsaturations and cyclic groups, wherein m is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or
 10. 75. A phase change ink composition according to claim 59 wherein R₂ is


76. A phase change ink composition according to claim 59 wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms.
 77. A phase change ink composition according to claim 1 wherein X is an alkyleneoxy group, an aryleneoxy group, an arylalkyleneoxy group, or an alkylaryleneoxy group.
 78. A phase change ink composition according to claim 1 wherein X is a group of the formula —(C_(a)H_(2a)O)bR₃ wherein a is an integer representing the number of carbon atoms in the alkyleneoxy group, b is an integer representing the number of repeat alkyleneoxy groups, and R₃ is a hydrogen atom, an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.
 79. A phase change ink composition according to claim 78 wherein a is 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, or
 50. 80. A phase change ink composition according to claim 78 wherein a is
 2. 81. A phase change ink composition according to claim 78 wherein a is
 3. 82. A phase change ink composition according to claim 78 wherein a is
 4. 83. A phase change ink composition according to claim 78 wherein b is at least
 1. 84. A phase change ink composition according to claim 78 wherein b is at least about
 2. 85. A phase change ink composition according to claim 78 wherein R₃ is a hydrogen atom.
 86. A phase change ink composition according to claim 78 wherein X is or


87. A phase change ink composition according to claim 78 wherein X is


88. A phase change ink composition according to claim 1 wherein X is a group of the formula

wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group.
 89. A phase change ink composition according to claim 88 wherein R₄ is a substituted alkyl group.
 90. A phase change ink composition according to claim 88 wherein R₄ is a substituted alkyl group.
 91. A phase change ink composition according to claim 88 wherein R₄ is an alkyl group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the alkyl group.
 92. A phase change ink composition according to claim 88 wherein R₄ is an alkyl group wherein no hetero atoms are present in the alkyl group.
 93. A phase change ink composition according to claim 88 wherein R₄ is an unsubstituted aryl group.
 94. A phase change ink composition according to claim 88 wherein R₄ is a substituted aryl group.
 95. A phase change ink composition according to claim 88 wherein R₄ is an aryl group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the aryl group.
 96. A phase change ink composition according to claim 88 wherein R₄ is an aryl group wherein no hetero atoms are present in the aryl group.
 97. A phase change ink composition according to claim 88 wherein R₄ is an unsubstituted arylalkyl group or an unsubstituted alkylaryl group.
 98. A phase change ink composition according to claim 88 wherein R₄ is a substituted arylalkyl group or a substituted alkylaryl group.
 99. A phase change ink composition according to claim 88 wherein R₄ is an arylalkyl group or an alkylaryl group wherein hetero atoms selected from oxygen, nitrogen, sulfur, silicon, or phosphorus are present in the arylalkyl group or alkylaryl group.
 100. A phase change ink composition according to claim 88 wherein R₄ is an arylalkyl group or an alkylaryl group wherein no hetero atoms are present in the arylalkyl group or alkylaryl group.
 101. A phase change ink composition according to claim 88 wherein R₄ is

wherein C₃₆H_(62+m) is a branched alkylene group which may include unsaturations and cyclic groups, wherein m is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or
 10. 102. A phase change ink composition according to claim 88 wherein R₄ is


103. A phase change ink composition according to claim 88 wherein R₄ is


104. A phase change ink composition according to claim 1 wherein the colorant of the formula

wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms,

wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms,

wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms,

or mixtures thereof.
 105. A phase change ink composition according to claim wherein the colorant is of the formula

wherein R₂ is a linear group having an average of about 50 carbon atoms, or mixtures thereof.
 106. A phase change ink composition according to claim 1 wherein the colorant is of the formula

or mixtures thereof, wherein C₃₆H_(62+m) is a branched alkylene group which may include unsaturations and cyclic groups, wherein m is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or
 10. 107. A phase change ink composition according to claim wherein the colorant is of the formula

wherein R₂ is a linear alkyl group having an average of about 50 carbon atoms.
 108. A phase change ink composition according to claim 1 wherein the colorant is of the formula

wherein Y and Y′ each, independently of the other, is a hydrogen atom or a bromine atom, n and n′ each, independently of the other, is an integer of 0, 1, 2, 3, or 4, R₁ and R₁′ each, independently of the other, is an alkylene group or an arylalkylene group, and X is (a) a group of the formula

wherein R₂ is an alkylene group, an arylene group, an arylalkylene group, or an alkylarylene group, (b) an alkyleneoxy group, an aryleneoxy group, an arylalkyleneoxy group, or an alkylaryleneoxy group, or (c) a group of the formula

wherein R₄ is an alkylene group, an arylene group, an arylalkylene group, or an alkylarylene group.
 109. A phase change ink composition according to claim 108 wherein n and n′ are each
 0. 110. A phase change ink composition according to claim 108 wherein n and n′ are each
 2. 111. A phase change ink composition according to claim 108 wherein R₁ and R₁′ each, independently of the other, is a substituted alkylene group or a substituted arylalkylene group.
 112. A phase change ink composition according to claim 108 wherein R₁ and R₁′ each, independently of the other, is an unsubstituted alkylene group or an unsubstituted arylalkylene group.
 113. A phase change ink composition according to claim 108 wherein R₁ and R₁′ are each of the formula


114. A phase change ink composition according to claim 108 wherein R₁ and R₁′ are each of the formula


115. A phase change ink composition according to claim 108 wherein X is a group of the formula

wherein R₂ is an alkylene group, an arylene group, an arylalkylene group, or an alkylarylene group.
 116. A phase change ink composition according to claim 115 wherein R₂ is a substituted alkylene group, a substituted arylene group, a substituted arylalkylene group, or a substituted alkylarylene group.
 117. A phase change ink composition according to claim 115 wherein R₂ is an unsubstituted alkylene group, an unsubstituted arylene group, an unsubstituted arylalkylene group, or an unsubstituted alkylarylene group.
 118. A phase change ink composition according to claim 115 wherein R₂ is

wherein C₃₆H_(62+m) is a branched alkylene group which may include unsaturations and cyclic groups, wherein m is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or
 10. 119. A phase change ink composition according to claim 115 wherein R₂ is


120. A phase change ink composition according to claim 108 wherein X is an alkyleneoxy group, an aryleneoxy group, an arylalkyleneoxy group, or an alkylaryleneoxy group.
 121. A phase change ink composition according to claim 120 wherein X is of the formula

wherein a is an integer representing the number of carbon atoms in the alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, b is an integer representing the number of repeat alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy groups, and R₃ and R₃′ each, independently of the others, is an alkylene group, an arylene group, an arylalkylene group, or an alkylarylene group.
 122. A phase change ink composition according to claim 108 wherein X is a group of the formula

wherein R₄ is an alkylene group, an arylene group, an arylalkylene group, or an alkylarylene group.
 123. A phase change ink composition according to claim 122 wherein R₄ is a substituted alkylene group, a substituted arylene group, a substituted arylalkylene group, or a substituted alkylarylene group.
 124. A phase change ink composition according to claim 122 wherein R₄ is an unsubstituted alkylene group, an unsubstituted arylene group, an unsubstituted arylalkylene group, or an unsubstituted alkylarylene group.
 125. A phase change ink composition according to claim 122 wherein R₄ is

wherein C₃₆H_(62+m) is a branched alkylene group which may include unsaturations and cyclic groups, wherein m is an integer of 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, or
 10. 126. A phase change ink composition according to claim 122 wherein R₄ is


127. A phase change ink composition according to claim 1 wherein the colorant is of the formula

wherein each Y, independently of the others, is a hydrogen atom or a bromine atom, each n, independently of the others, is an integer of 0, 1, 2, 3, or 4, and each R₁, independently of the others, is an alkylene group or an arylalkylene group, said moieties being linked by a central atom or group of atoms or bonded to a polymeric chain.
 128. A process which comprises (1) incorporating into an ink jet printing apparatus a phase change ink composition comprising a phase change ink carrier and a colorant compound of the formula

wherein Y is a hydrogen atom or a bromine atom, n is an integer of 0, 1, 2, 3, or 4, R₁ is an alkylene group or an arylalkylene group, and X is (a) a hydrogen atom, (b) a group of the formula

wherein R₂ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group, (c) an alkyleneoxy, aryleneoxy, arylalkyleneoxy, or alkylaryleneoxy group, or (d) a group of the formula

wherein R₄ is an alkyl group, an aryl group, an arylalkyl group, or an alkylaryl group; (2) melting the ink; and (3) causing droplets of the melted ink to be ejected in an imagewise pattern onto a substrate.
 129. A process according to claim 128 wherein the printing apparatus employs a piezoelectric printing process wherein droplets of the ink are caused to be ejected in imagewise pattern by oscillations of piezoelectric vibrating elements.
 130. A process according to claim 128 wherein the substrate is a final recording sheet and droplets of the melted ink are ejected in an imagewise pattern directly onto the final recording sheet.
 131. A process according to claim 128 wherein the substrate is an intermediate transfer member and droplets of the melted ink are ejected in an imagewise pattern onto the intermediate transfer member followed by transfer of the imagewise pattern from the intermediate transfer member to a final recording sheet.
 132. A process according to claim 131 wherein the intermediate transfer member is heated to a temperature above that of the final recording sheet and below that of the melted ink in the printing apparatus. 